Durastar DS2010聚合物含有一种脱模剂。它外观极好,几乎是水清澈的。其最突出的特点是韧性、耐化学性和优良的加工特性。DS2010具有很好的韧性,如Izod抗冲击性所示。暴露在芳香油中往往会导致许多聚合物树脂开裂或实际断裂,但DS2010暴露在这些油中时仍保持其物理性能,其外观几乎没有变化。易于加工,流动容易,填充复杂的模具。根据现行的美国食品药品管理局(FDA)法规,Durastar DS2010可用于符合21 CFR 177.1240规范和使用条件的食品接触物品。本产品经ANSI/NSF标准51认证。 Durastar™ DS2010 polymer contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. DS2010 has very good toughness as shown by Izod impact resistance. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS2010 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily and fills intricate molds. Under existing United States Food and Drug Administration (FDA) regulations, Durastar™ DS2010 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240. This product is certified to ANSI/NSF Standard 51. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.19 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.20 to 0.60 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
60 | J/m | ASTM D256 |
23℃ 23℃ |
370 | J/m | ASTM D256 |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-40℃ -40℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4812 | ||
-40℃ -40℃ |
ASTM D4812 | ||
23℃ 23℃ |
ASTM D4812 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-40℃,Energy at Peak Load -40℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-40℃,能量到力量峰值 -40 ℃, energy to peak strength |
J | ISO 6603-2 | |
23℃,能量到力量峰值 23 ℃, energy to peak strength |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 2 |
|||
23℃ 23℃ 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
23 ℃,1 kHz 23 ℃,1 kHz |
ASTM D150 | ||
23 ℃,10 kHz 23 ℃,10 kHz |
ASTM D150 | ||
23 ℃,100 kHz 23 ℃,100 kHz |
ASTM D150 | ||
23 ℃,1 MHz 23 ℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
23℃,1 kHz 23℃,1 kHz |
ASTM D150 | ||
23℃,10 kHz 23℃,10 kHz |
ASTM D150 | ||
23℃,100 kHz 23℃,100 kHz |
ASTM D150 | ||
23℃,1 MHz 23℃,1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.0 mm,AT 3.0 mm,AT |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
ASTM D1003 | ||
总计 total |
% | ASTM D1003 | |
Regular Regular |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
工企利润增66.9% 七成行业盈利超疫情前
2021-07-28 搜料网资讯: 7月27日,国家统计局发布2021年上半年工业企业利润数据。 今年1~6月份,全国规模以上工业企业实现利润总额42183.3亿元,同比增长66.9%,比2019年1~6月份增长45.5%,两年平均 |
工企利润增66.9% 七成行业盈利超疫情前 搜料网资讯:7月27日,国家统计局发布2021年上半年工业企业利润数据。 今年1~6月份,全国规模以上工业企业实现利润总额42183.3亿元,同比增长66.9%,比2019年1~6月份增长45.5%,两年平均增长20.6%。其中,二季度规模以上工业企业利润同比增长36.0%,比2019年同期增长42.5%,两年平均增长19.4%。 6月份,规模以上工业企业实现利润总额7918.0亿元,同比增长20%。 国家统计局工业司高级统计师朱虹指出,2021年上半年,随着国民经济稳中加固稳中向好,工业生产需求稳定恢复,企业经营状况持续改善,企业利润平稳较快增长。
数据来源:国家统计局 采矿业等企业利润增长明显 朱虹指出,数据显示,七成行业盈利超过疫情前水平。上半年,在41个工业大类行业中,有40个行业利润同比增长(或扭亏为盈),1个行业同比持平。其中,有36个行业利润实现两位数及以上增长,占87.8%;有7个行业增速超过100%。与2019年同期相比,有29个行业利润实现增长,占70.7%。 记者注意到,上半年,上游采矿业和原材料制造业企业利润增长明显。采矿业、原材料制造业利润同比分别增长1.33倍、1.83倍,对规模以上工业利润增长的贡献率合计为58.9%,利润两年平均增速分别为16.5%、35.8%。 值得注意的是,之前一段时间上游大宗商品价格上涨造成的影响因素有所削弱。 红塔证券研究所所长李奇霖对记者分析,分大类行业来看,6月采矿业当月利润率为18%,前值为20%,采矿业利润率有所下行,这可能是因为在大宗商品价格调整政策的引导下,6月部分大宗商品价格有所回落。 不过,李奇霖也向记者指出,大宗商品价格的传导存在时滞,虽然5月下旬大宗商品价格出现了明显回调,但是6月企业使用的原材料可能是4~5月购入的,包含了前期高价购入的原材料。 因此,从最新工企利润数据看,在制造业方面,6月当月制造业利润率为6.72%,前值为7.62%,制造业利润率下行明显。这可能与上游原材料价格上涨导致的行业成本增加相关。 企业资产负债状况改善 最新工企利润数据还显示,目前企业经营状况持续改善。 上半年,规模以上工业企业营业收入同比增长27.9%,增速分别比营业成本、费用合计快1.5和9.2个百分点。单位成本费用同比双双下降,每百元营业收入中的成本同比减少0.98元,其中,采矿业、原材料制造业分别减少6.79元、2.64元;每百元营业收入中的费用同比减少0.65元。规模以上工业企业营业收入利润率为7.11%,同比提高1.66个百分点,比一季度提高0.47个百分点。 开源证券首席经济学家赵伟则对记者表示,6月数据显示,限产影响下,上游行业利润增速回落,中下游利润增速结构分化。 6月,上游行业中的煤炭和钢铁受限产影响,利润两年复合增速分别为27.3%、18.9%,低于5月增速29.7%、39.7%;中下游行业中,医药制造、电气机械、专用设备受益于出口改善,利润增速抬升,而汽车由于销售增速下滑明显,拖累利润增长。 数据还显示,当前亏损企业数量减少,亏损额下降。6月末,规模以上工业企业亏损面为22.5%,同比缩小2.4个百分点,比3月末缩小4.6个百分点;上半年,亏损企业亏损额同比减少23.5%。企业亏损情况较去年同期明显改善。 此外,资产负债状况改善,企业发展更加稳健。6月末,规模以上工业企业资产同比增长9.3%,所有者权益增长10.3%,均实现较快增长。规模以上工业企业资产负债率为56.5%,同比降低0.4个百分点。其中,国有控股企业资产负债率为57.0%,同比降低0.5个百分点。 朱虹指出,总体来看,上半年工业企业盈利稳定恢复,经营状况持续改善。但也要看到,企业效益恢复不平衡状况依然存在,私营、小微企业盈利恢复相对较慢,大宗商品价格持续高位运行挤压企业盈利空间,产业链供应链还存在短板弱项。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。