牌号简介 About |
---|
TOPAS 6013M-07是一种注塑级,具有宽加工窗口,特别适用于包括IBM和ISBM在内的吹塑工艺。它是一种玻璃透明的无定形聚合物,具有出色的防潮性,耐化学性,高纯度和非反应性表面,使其成为医疗保健和其他高科技产品的最佳选择。较低的可浸出物和TOPAS COC的可萃取物可保持内容物的稳定性和质量。它是一种非极性基质,不像玻璃罐那样促进吸附,变性,聚集或沉淀。该等级具有高(130°C)热变形温度,可承受121°C蒸汽灭菌协议,以及伽玛和EtO程序。 注塑成型,医疗保健,光学和诊断的相关等级 TOPAS 6015S-04 - 134°C协议的更高热变形温度(150°C) TOPAS 6017S-04 - 我们最耐热变形的IM级(HDT = 170°C) TOPAS 5013L-10 - 高流动等级; 润滑版,提供更好的加工多功能性 TOPAS 5013S-04 - 高流动等级,无润滑剂 TOPAS® 6013M-07 Product Description TOPAS 6013M-07 is an injection molding grade with a wide processing window, especially suited for blow molding processes including IBM and ISBM. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve content stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high (130°C) heat distortion temperature to withstand 121°C steam sterilization protocols, as well as gamma and EtO procedures. Selected Applications Drug delivery Prefilled syringes, vials, cartridges Bottles and tubes Surgical instruments IV containers and components Labware Optics Electronics Food packaging Healthcare and food contact Leading Attributes Low leachables & extractables, low water transmission Non-ionic, does not promote adsorption like glass Minimally reactive Chemically resistant to alcohol, acetone, and acrylates Transparent, withstands EtO/gamma/steam sterilization Temperature resistance, clarity and purity Clarity, low birefringence, low moisture sensitivity Low dielectric constant, thermoplastic Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Injection Molding, Healthcare, Optics and Diagnostics TOPAS 6015S-04 - higher heat distortion temperature (150°C) for 134°C protocols TOPAS 6017S-04 - our most heat distortion resistant IM grade (HDT=170°C) TOPAS 5013L-10 - high flow grade; lubricated version for greater processing versatility TOPAS 5013S-04 - high flow grade without lubricant TOPAS® 6013M-07 TOPAS® 6013M-07 is a Cyclic Olefin Copolymer (COC) product. It is available in Africa & Middle East, Asia Pacific, or Latin America. Characteristics include: Copolymer Good Aesthetics |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,2.16kg 260℃,2.16kg |
12 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,2.16 kg 260℃,2.16 kg |
13.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
0.50 到 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.010 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
% | ISO 13468-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Dependent on process conditions and part design. |
3 10°C/min |
【新闻资讯】查看全部
帝人开设塑料回收设施,生产再生聚酯颗粒
2021-10-27 搜料网资讯: 帝人集团作为以材料为主的制造业公司,为了实现循环型社会,一直在致力于3R(Reduce、Reuse、Recycle)工作。 总部位于东京的纤维和产品加工公司 Teijin Frontier Co.(以下简 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |