牌号简介 About |
---|
概述PULSE™ GX50是一种易于流动、中等热量、低光泽和低密度的PC/ABS树脂,为汽车内饰部件应用提供了最佳性能。优点:光泽度低,允许油漆不太可见的应用低密度行驶到更轻和成本优化的零件易于流动、减少废料和更快的循环时间,同时使薄壁零件的设计质量降低高冲击强度,即使在低温耐热性下,对大多数汽车内饰部件进行了优化。支架自然白颜色在与颜色浓缩物(自着色)或Trinseo Color Masterbatch技术一起使用时产生高质量的零件外观低气味和VOC,以满足所有全球汽车OEM规范应用中(地板)控制台下仪表板部件门板装饰柱存储/装载地板/手套箱 Overview PULSE™ GX50 is an easy flow, medium-heat, low gloss and low density PC/ABS resin delivering optimized performance for automotive interior component applications. Benefits Low gloss allowing paint-less visible applications Low density driving to lighter and cost optimized parts Easy flow, reduced scrap, and faster cycle times, while enabling thin wall part design for mass reduction High-impact strength even at low temperature Heat resistance optimized for the majority of automotive interior components Consistent natural white color produces high quality part appearance when used with color concentrates (self coloring) or Trinseo Color Masterbatch Technology Low odor & VOC to meet all global Automotive OEM specifications Applications Mid (floor)consoles Lower Instrument Panel components Door panel trim Pillars Storage / load floors / glove box |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.09 | g/cm³ | ISO 1183/B |
表观密度 Apparent density |
0.63 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
12 | g/10min | ISO 1133 |
螺旋流动长度 Spiral flow length 2 |
58.0 | cm | |
收缩率 Shrinkage rate |
0.40 到 0.70 | % | ISO 294-4 |
VOC Content VOC Content |
µg/g | VDA 277 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~80℃ MD:-30~80℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 熔体温度: 500°F, 注塑压力: 2.61E+4 psi |
3 0.039 in/min |
【新闻资讯】查看全部
创新技术为食品软包装开启全新市场机遇
2016-11-18 现代食品包装不仅为食品及内容物提供物理保护,还可帮助延长食品的保质期、提供产品信息并展示品牌形象、更加方便消费者日常使用。相较于其他包装材质和形式,如玻璃、金属及硬塑包装等,软塑包装更加环保、节省原材料和运输成本,从而更好地满足了现代包装工业的需求。 现今的包装生产企业,一方面要满足不断增长的对于食品饮料包装个性化、高品质的需求;另一方面,还要探索如何在市场变革中寻求创新,从而实现能耗的降低,效益的提高。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |