| 牌号简介 About |
|---|
| Hifax CA 721 GW是一种柔性聚丙烯树脂，专门为我们的客户开发用于防水应用。它是使用利安德巴塞尔专有的加泰罗尼亚工艺技术制造的。Hifax CA 721 GW膜可以在槽模挤出机、圆模（吹膜）挤出机和大多数压延设备（如用于PVC）上生产。如果需要，膜可以加固和变形。Hifax CA 721 GW以天然颗粒形式提供，预先稳定，可长期暴露于高温和紫外线下。我们的客户规定Hifax CA 721 GW的典型应用包括饮用水安全壳和输送系统、鱼塘衬里、雪塘、隧道衬里、水库衬里和浮盖、食品相关衬里和紫外线暴露饮用水应用。 Hifax CA 721 GW is a flexible polypropylene resin used by our customers for waterproofing applications. It is manufactured using the LyondellBasell's proprietary Catalloy process technology. Hifax CA 721 GW membranes can be produced on slot die extruders, circular die (Blown film) extruders and on most of the calendering units. Hifax CA 721 GW is available in natural pellet form, and is UV light stabilised. Our customers use Hifax CA 721 GW to produce flexible membrane, fish pond liner, snow lagoon membrane, tunnel lining, water reservoir liner, floating cover, soil and waste sheet and flexible profiles. Hifax CA 721 GW is not intended for medical and pharmaceutical applications. |
产品描述 Product Description
用途：土工膜;衬里;容器;管道系统;
颜色：自然色
加工条件：压延
性能特点： 热稳定性好; 耐化学性; 耐低温冲击; 耐臭氧; 韧性好; 耐候抗UV; 抗应力开裂; 热封性好; 抗穿孔性; Weather resistance is good,Good flexibility,Good heat sealing,Ozone resistance,Solvent resistance,low-temperature impact resistance,Puncture Resistant,Heat Stabilized,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.880 | g/cm³ | ISO 1183/A |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
0.60 | g/10min | ISO 1133 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
70 ℃ 70 ℃ |
> 1000 | hr | ASTM D5397 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
0℃ 0℃ |
无断裂 | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
韧性/脆性转变温度 Toughness/brittle transition temperature |
-55.0 | ℃ | 内部方法 |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Critical Cone Height（1.00 mm） Critical Cone Height（1.00 mm） 1 |
mm | 内部方法 | |
|
Multi-axial Burst Stress（1.00 mm） Multi-axial Burst Stress（1.00 mm） |
% | ASTM D5617 | |
|
耐臭氧性 Ozone resistance |
ASTM D2137 | ||
|
Resistance to Microorganisms Resistance to Microorganisms |
DIN 53739 | ||
|
Resistance to Root Penetration Resistance to Root Penetration 2 |
|||
|
氙老化测试机 Xenon aging testing machine 3 |
|||
|
1.00 mm 1.00 mm 3 |
yr | DIN 53387 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
拉伸强度 tensile strength |
|||
|
屈服，23℃，1 mm Yield, 23 ℃, 1 mm |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃，1.00 mm Fracture, 23 ℃, 1.00 mm |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
撕裂阻力 Tear resistance |
|||
|
1.00 mm 1.00 mm |
kN/m | ASTM D1004 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 GR1/GM3 |
| 3 FLL Test |
| 4 1AX, 1 mm black/white sheets |
|
【新闻资讯】查看全部 
陶氏将在美扩建MA产能
2021-09-04 搜料网资讯： 日前，陶氏将在美国墨西哥湾沿岸投资扩建5万吨/年的丙烯酸甲酯(MA)生产能力。新产能位于路易斯安那州圣查尔斯市，计划2022年上半年投产，重点满足北美市场需求。 该 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付