| 牌号简介 About |
|---|
| Ixef BXT-2000/0203树脂专用于挤出和吹塑加工。与其它专门针对注射成型牌号不同， Ixef BXT-2000/0203树脂可成功地挤出成管件、管材、片材、膜，以及吹塑成各种型材。 BXT-2000/0203树脂能成功耐受大多数汽车流体和燃料渗透性。同时具有低吸湿性、良好的尺寸稳定性和耐化学性，以及优异的机械性能。 - 本色： Ixef BXT-2000/0203 Ixef® BXT 2000-0203 resin was developed specifically for extrusion and blow-molding processes. Unlike grades targeted for injection molding, Ixef® BXT 2000-0203 resin can be successfully extruded into tube, pipe, sheet and film and blow-molded into various profiles. BXT 2000-0203 resin has proven permeation resistance to most automotive fluids and fuels. It also offers low moisture absorption, excellent dimensional stability, and chemical resistance as well as outstanding mechanical properties. Natural: Ixef® BXT 2000-0203 |
产品描述 Product Description
用途：薄膜;片材;吹塑成型应用;管件;管道系统;
颜色：自然色
加工条件：挤出 Extrusion
性能特点： 低吸湿性; 尺寸稳定性好; 耐化学性; 阻隔树脂; 流动性高; 韧性好; 耐燃油; 表面光泽度好; Good flexibility,Good surface appearance,Good Dimensional Stability,High liquidity,Block resin,Solvent resistance,Low moisture absorption,Fuel resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.12 | g/cm³ | ISO 1183 |
|
表观密度 Apparent density |
0.70 | g/cm³ | ASTM D1895B |
|
Melt Flow（240℃） Melt Flow（240℃） |
6.00 | g/10 min | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
2470 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
39.9 | MPa | ASTM D638 |
|
屈服 yield |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2 | |
|
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2 | |
|
Modulus of Elasticity Modulus of Elasticity |
GPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Permeation - CE 10 Fuel（60℃） Permeation - CE 10 Fuel（60℃） |
g·mm/m²/atm/24 hr | SAE J2659 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4812 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature |
℃ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
路博润德克萨斯州聚异丁烯项目破土开工
2017-04-05 3月22日，路博润在美国德克萨斯州鹿园新建的聚异丁烯(PIB)厂区破土动工。 根据路博润之前公布的10年分阶段投资计划，将持续改造其添加剂基础设施，而此厂区的建设正是其中一项举措。 新厂区预计在2019年上半年全面投入使用。 它将为路博润提供高反应性聚异丁烯(HR PIB)生产能力，这种聚异丁烯是下一代分散剂和润滑剂的关键原料。 来源 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付