牌号简介 About |
---|
Kalix® 9950是一种50%玻璃纤维增强高性能聚酰胺。它是一种热水可塑性材料,适用于要求优良机械性能和表面质量的部件。Kalix® 9950具有高刚度和强度、很好的冲击性能、良好的尺寸稳定性、低翘曲性能和良好的表面光洁度。它可以成功地电镀,例如用不导电的真空金属化,或用软接触或紫外线面漆涂漆。有关合适的电镀和喷漆系统的更多信息,请联系您的Solvay专业聚合物销售代表。Kalix® 9950具有高流量、低闪光倾向和快速循环时间的优良组合,使其成为大量生产的薄壁零件的成本竞争选择,例如移动电子设备中的结构零件。黑色:Kalix® 9950黑色000白色:Kalix® 9950白色000自然色:Kalix® 9950 NT 000 Kalix® 9950 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties and excellent surface quality. Kalix® 9950 is characterized by high stiffness and strength, very good impact properties, good dimensional stability, low warpage behavior and excellent surface finish. It can be successfully plated, for example with non conductive vacuum metallization, or painted with soft touch or UV top coat paints. Please contact your Solvay Specialty Polymers sales representative for more information on suitable plating and painting systems. Kalix® 9950 exhibits an excellent combination of high flow, low flash tendency and fast cycle time which makes it a cost-competitive option for thin-walled parts produced in large quantities, such as structural parts in mobile electronic devices. Black: Kalix® 9950 BK 000 White: Kalix® 9950 WH 000 Natural: Kalix® 9950 NT 000 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.60 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate 3 |
内部方法 | ||
TD TD |
0.32 | % | 内部方法 |
MD MD |
0.13 | % | 内部方法 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.37 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
18500 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant 4 |
ASTM D2520 | ||
1.00 GHz 1.00 GHz |
ASTM D2520 | ||
2.40 GHz 2.40 GHz |
ASTM D2520 | ||
耗散因数 Dissipation factor 4 |
ASTM D2520 | ||
1 GHz 1 GHz |
ASTM D2520 | ||
2.4 GHz 2.4 GHz |
ASTM D2520 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.60 mm,所有颜色 0.60 mm, all colors |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 索尔维测试方法。收缩率会根据部件的设计和加工条件而改变。请接洽索尔维技术代表,获取更多信息。 |
3 方法 B |
【新闻资讯】查看全部
联合国以为塑料回收行业表现不佳,需求重塑
2019-01-07 近日,联合国环境署发布一篇文章“Plastic recycling: an underperforming sector ripe for a remake”,认为塑料回收行业表现不佳,需要重塑! 联合国认为,到目前为止对于解决塑料涌入我们海洋还没有强有力的方案,但回收必须成为方案的一部分。许多专家认为,问题在于当前的流程不适合我们的目的。 全世界每年生产约3亿吨塑料废物。迄今为止,只有9%的塑料废物被回收利 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |