牌号简介 About |
---|
玻璃纤维增强邻苯二甲酸二烯丙酯模塑料具有良好的机械强度,在湿热条件下具有较高的电绝缘性能,即使在恶劣的环境条件下也具有优异的尺寸稳定性,易于在长流道系统中使用。主要用途:连接器、线轴、电位器、开关。本产品符合重金属和PCA的允许上限,并符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)的要求。 Glass-fibre reinforced diallyl phthalate moulding compound Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensional stability even under severe environmental conditions, easy flowing for use in long runner systems. Primary application(s): Connectors, Bobbins, Potentiometers, switches This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.80 到 2.00 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.75 到 0.90 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate 3 |
|||
MD MD 3 |
0.15 到 0.45 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.20 | % | ISO 62 |
后收缩 Post contraction 4 |
< 0.050 | % | ISO 2577 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
注塑成型 injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
3 168 h / 110°C |
【新闻资讯】查看全部
CFRP极受高端用户欢迎但如何降低本钱仍需应战
2016-03-21 CFRP是一种碳纤维轻量化材料,能显著减轻产品的重量,因此它是提高能源利用效率理想材料之一。由于CFRP材料具备的优良属性,包括高刚性和高强度属性,促进该材料市场有增长的趋势。然而CFRP材料制造费时费力,当碳纤维与树脂材料浸渍配制后,要完全烘烤固化成型需5小时;而将聚丙烯腈原丝经1300℃高温碳化成碳纤维更要耗费大量热能,因此高成本仍将是影响其发展的主要挑战因素。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |