| 牌号简介 About |
|---|
| 乐天贝斯皮尔2407是一种现成的热塑性复合材料，旨在使剥离热密封层到各种基板。基树脂是乙烯与丙烯酸甲酯的无规共聚物，在高压釜反应器中经高压聚合而成。介绍了改性工艺，以保证不同薄膜工艺的最佳加工性能，以及合适的热封和剥离性能。应用LOTRYL BESTPEEL 2407用作层压板的顶层，以便在各种基材（如PP、PS、PET和PVC）上提供热密封性，并易于通过界面剥离打开。采用共挤镀膜、铸膜共挤、吹膜共挤或片材共挤等工艺，可方便地加工出洛特利贝斯皮尔2407，可直接或与其它薄膜复合后，制成可作为盖子的多层膜。 LOTRYL® BESTPEEL 2407 is a ready-to-use thermoplastic composition designed to make peelable heat seal layers onto various substrates. The base resin is a random copolymer of ethylene and methyl acrylate, polymerized by high-pressure process in autoclave reactor. Modification is introduced to ensure the best processability in the different film technologies, and the suitable properties in heat sealing and peeling. Applications LOTRYL® BESTPEEL 2407 is used as top layer of laminates in order to provide the functions of heat sealability onto various substrates like PP, PS, PET and PVC, and easy opening by interfacial peeling. LOTRYL® BESTPEEL 2407 is easily processed using the technologies of coextrusion coating, cast film coextrusion, blown film coextrusion or sheet coextrusion, to produce multilayers that can be used as lids, either directly or after lamination with other films. |
产品描述 Product Description
用途：薄膜;片材;密封件;盖子;层压板;
加工条件：涂层
性能特点： 无规共聚物; 耐高压加热性; 热封性好; 易加工; Excellent Processability,Good heat sealing,Random copolymer,High pressure heat resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.940 | g/cm³ | ASTM D1505 |
|
密度 Density |
0.940 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
6.0 to 8.0 | g/10min | ASTM D1238 |
|
190℃，2.16kg 190℃，2.16kg |
6.0 to 8.0 | g/10min | ISO 1133 |
|
甲基丙烯酸含量 Methacrylic acid content |
23.0 to 25.0 | wt% | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A，模压成型 Shaw A, molded |
ASTM D2240 | ||
|
邵氏 A，模压成型 Shaw A, molded |
ISO 868 | ||
|
拉伸强度 tensile strength |
|||
|
断裂，模压成型 Fracture, molded |
MPa | ISO 527-2 | |
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，模压成型 Fracture, molded |
% | ISO 527-2 | |
|
断裂，模压成型 Fracture, molded |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
模压成型 Compression Molding |
MPa | ASTM D790 | |
|
模压成型 Compression Molding |
MPa | ISO 178 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
瓦克集团上调化工原料无机硅、硅油等产品价钱
2017-10-16 德国化工集团瓦克(Wacker)宣布，自2017年11月1日起，上调化工原料有机硅聚合物、硅油以及其他还处在生产阶段的有机硅相关产品的价格。本次价格的上调也涉及到了以HDK品牌销售的气相二氧化硅等产品的售价。根据产品系列、地区以及业务领域的差异，只要现有的客户所签署的合同允许，价格提升的幅度最高可以达到25%。而原材料以及能源成本的上涨而造成的生产成本大幅度增加是瓦克采取这一措施的主要原因。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付