牌号简介 About |
---|
EMERGE™ PC/ABS 7100 高性能树脂很好地平衡了材料的抗冲击性能、耐热性能和加工性能。其良好的基材颜色和批次间的颜色稳定性使其特别适宜生产要求色差小的部件。这种树脂的流动性优异,特别适宜于诸如便携式电子设备等薄壁结构产品的注塑加工。 EMERGE™ PC/ABS 7100 advanced resin exhibits a balance of properties between impact strength, heat resistance and processability. Its superior natural base color and lot-to-lot color consistency makes it ideally suited for producing very consistent colored parts. It has excellent flow and is ideal for injection molding in thin-wall applications, such as portable electronic devices. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.11 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
230℃,3.80kg 230℃,3.80kg |
4.5 | g/10min | ASTM D1238 |
260℃,5.0kg 260℃,5.0kg |
25 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃,3.2mm,注塑成型 -30 ℃, 3.2mm, injection molding |
290 | J/m | ASTM D256 |
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,3.2 mm,注塑成型 0.45 MPa, unannealed, 3.2 mm, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm,注塑 1.8 MPa, unannealed, 3.2 mm, injection molded |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.00 mm 1.00 mm 5 |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
干燥温度 drying temperature |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级,3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D638 | |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 标准 B (120°C/h), 压 力1 (10N) |
4 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
改性塑料研发“刚度”“柔度”成重要目的
2016-04-11 “刚度”是指物体发生单位形变时所需要的力的大小;“柔度”则指物体在单位力下所发生的形变大小。 可以看出,“刚度”越大的物体,越不容易发生变形(表现在伸长率很小);“柔度”越大的物体越容易发生变形(表现在伸长率较大)。一种理想状态,物体的刚度趋近于无穷大(或者物体受力作用其变形小到可以忽略的程度),我们就称该物体为刚体。在力学分析时,可以不考虑其自身形变。因此,刚性是反映物体形变难易程度的一个属性。韧性的材料比较柔软,物性表的拉伸断裂伸长率、抗冲击强度较大;硬度、拉伸强度和拉 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |