牌号简介 About |
---|
Vibrathane B670是一种以聚醚为基础的MDI端接预聚物,用1,4-丁二醇固化后,得到53-shore D氨基甲酸乙酯。Vibrathane B670具有极低的粘度和出色的加工特性。由Vibrathane B670制成的聚氨酯:具有优异的低温性能、高耐磨性、出色的水解稳定性、高撕裂强度。 VIBRATHANE B670 is a polyether-based MDI terminated prepolymer which yields a 53 Shore D urethane when cured with 1,4-butanediol. VIBRATHANE B670 is characterized by exceptionally low viscosity and outstanding processing characteristics. Urethanes made from VIBRATHANE B670: Exhibit excellent low temperature properties High abrasion resistance Outstanding hydrolytic stability High tear strength |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
51.7 | MPa | ASTM D412 |
100% 应变 100% strain |
15.9 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
380 | % | ASTM D412 |
撕裂强度 tear strength |
|||
-- -- 2 |
131 | kN/m | ASTM D624 |
开裂 cracking |
30 | kN/m | ASTM D470 |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
脱模时间 stripping time |
min | ||
后固化时间 Post curing time |
|||
110℃ 110℃ |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
压缩强度 compressive strength |
ASTM D695 | ||
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
八部门联合印发《“十四五”智能制造发展规划》
2021-12-30 搜料网资讯: 近日,工业和信息化部、国家发展和改革委员会、教育部、科技部、财政部、人力资源和社会保障部、国家市场监督管理总局、国务院国有资产监督管理委员会等八部门联 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |