牌号简介 About |
---|
CALIBRE™ MEGARAD™ 2081-15聚碳酸酯树脂为最终用户提供了辐射灭菌的医疗器械,使其颜色更接近天然树脂的清水外观。当暴露在高能辐射(γ或电子束)下时,CALIBRE™ MEGARAD™ 2081-15树脂比一般用途的聚碳酸酯树脂可减少50%的变色。Calibre 2081-15树脂已根据ISO 10993(医疗器械生物学评估)进行了生物相容性测试,适用于批准的医疗应用。主要特点:在ISO 10993下测试的高能量辐射稳定透明包含模具释放应用:医疗应用 CALIBRE™ MEGARAD 2081-15 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to high energy radiation (gamma or electron beam), CALIBRE MEGARAD 2081-15 resin can reduce the color shift by 50% compared to general purpose polycarbonate resins. CALIBRE 2081-15 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Stabilized for higher energy radiation Tested under ISO 10993 Transparent Contains mold release Applications: Medical applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.20 | g/cm³ | ASTM D792,ISO 1183-A |
-- -- |
1.2 | g/cm³ | ISO 1183-4 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
15 | g/10min | ASTM D1238,ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
12.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
ASTM D570 , ISO 62 | ||
23℃,24hr 23℃,24hr |
% | ASTM D570,ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570,ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA 4 | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA 4 | |
简支梁冲击强度 Charpy impact strength |
ISO 179/1eU 4 | ||
-30℃ -30℃ |
ISO 179/1eU 4 | ||
23℃ 23℃ |
ISO 179/1eU 4 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ASTM D256 , ISO 180 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 9 |
|||
23℃,总能量 23 ℃, total energy 9 |
J | ASTM D3763 | |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 4 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 4 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 10 | |
B50 B50 |
℃ | ISO 306 | |
B50 B50 |
℃ | ISO 306 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-40 到 82℃ -40 to 82 ℃ |
cm/cm/℃ | ASTM D696 | |
-- -- |
cm/cm/℃ | ISO 11359-2 4 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
-- -- |
ohms·cm | ASTM D257 | |
-- -- |
ohms·cm | IEC 60093 4 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 4,IEC 60243-1 4 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 , IEC 60250 4 | ||
100 Hz 100 Hz |
IEC 60250 4 | ||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 , IEC 60250 4 | ||
100 Hz 100 Hz |
IEC 60250 4 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
ISO 1210 4 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 , ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 5 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/50 , ISO 527-2 4 | |
拉伸强度 tensile strength |
|||
屈服 yield 5 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 , ISO 527-2 4 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 5 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 , ISO 527-2 4 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 4 | |
弯曲模量 Bending modulus |
|||
-- -- 6 |
MPa | ASTM D790 | |
-- -- 7 , 8 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 6 |
MPa | ASTM D790 | |
-- -- 7 , 8 |
MPa | ISO 178 | |
耐磨耗性 Wear resistance |
% | ASTM D1044 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
ISO 1210 4 |
备注 |
---|
1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
2 一般属性:这些不能被视为规格。 |
3 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
4 2.0 in/min |
5 方法 I (三点负荷), 0.079 in/min |
6 0.079 in/min |
7 3 点 |
8 11.1 ft/sec |
9 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
海运大塞港,空运价格暴涨,但“即使是很小运力转移也会挤爆空运”
2021-12-27 搜料网资讯: 当空运价格已经仅是海运价格的3倍时,货主是否会想出新的货运排列组合玩法,改变供应链运输格局? 不过,在过去三个月里,从中国到美国的主要航空货运航线的价格 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |