牌号简介 About |
---|
Texin® HM-1206树脂是一种透明的高性能热塑性聚氨酯,具有标准工程热塑性塑料的硬度和模量。 |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PUR PUR
颜色:清晰/透明
加工条件:挤出 Extrusion
性能特点: 低吸湿性; 耐磨; 耐化学性; 耐高温; 热膨胀系数低; 收缩性低; 冲击性能好; Low CLTE,High impact resistance,Low contractility,High Heat Resistance,Good wear resistance,Solvent resistance,Low moisture absorption
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.24 | g/cm³ | ASTM D792 |
密度 Density |
1.24 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:2.54 mm MD:2.54 mm |
0.50 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.17 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
-30℃,3.2mm -30℃,3.2mm |
ASTM D256 | ||
23℃,3.2mm 23℃,3.2mm |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed 3 |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed 3 |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
ASTM D1525 4 | ||
A50 A50 |
ISO 306/A50 | ||
A50 A50 3 |
℃ | ISO 306/A50 | |
A50 A50 |
℃ | ISO 306/A50 | |
-- -- 3 |
℃ | ASTM D1525 4 | |
-- -- |
℃ | ASTM D1525 4 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
|||
3180 µm 3180 µm |
% | ISO 3583 | |
3180 µm 3180 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3180 µm 3180 µm |
% | ISO 3583 | |
3180 µm 3180 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
-- -- |
MPa | ASTM D790 | |
-- -- 2 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
-- -- |
MPa | ISO 178 | |
-- -- 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弯曲应变 - at Maximum Stress Bending strain - at Maximum Stress |
|||
-- -- |
% | ISO 178 | |
-- -- |
% | ASTM D790 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
洛氏硬度 Rockwell hardness |
ISO 2039-2 | ||
M 级 M-level |
ISO 2039-2 | ||
R 级 R-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 at 5% Strain |
3 Post-cured for 2 hours at 230°F |
4 速率 A (50°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
五建公司承建斯尔邦丙烯腈装置中交
2021-12-13 搜料网资讯: 11月30日,炼化工程集团五建公司承建的连云港斯尔邦石化二期丙烷产业链项目丙烯腈装置实现高标准中交。 该装置是业主斯尔邦石化打造新能源新材料产业集群的重点工 |
五建公司承建斯尔邦丙烯腈装置中交 搜料网资讯:11月30日,炼化工程集团五建公司承建的连云港斯尔邦石化二期丙烷产业链项目丙烯腈装置实现高标准中交。 该装置是业主斯尔邦石化打造新能源新材料产业集群的重点工程。项目团队克服土建地质情况复杂、高温多雨等不利因素,精心策划、科学统筹、合理安排现场施工。强化安全质量管理工作,实现270万安全人工时,现场焊接一次拍片合格率达98.51%。项目部获得徐圩新区工程建设有功单位、保障农民工工资先进单位等多项荣誉。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。