牌号简介 About |
---|
TN7006是一种低密度聚乙烯(LDPE),专门为共挤薄膜和层压而开发。该树脂在机械、光学和刚度性能方面具有很大的结合。此外,TN7006凝胶含量低,保证了生产出优良的外观膜。根据ASTM D-4976-04A标准规范,本产品为PE 114。添加剂:无添加剂应用:用于共挤食品包装的高清晰度薄膜,如:奶酪、肉类、香肠、火腿片等。用于桌布、窗帘和层压组织的铸膜。卫生和清洁用固体、液体或糕点产品的软瓶子。 TN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides TN7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. Additives: No additives Application: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness. Process: Blown Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.60 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
2% 正割,TD,40 µm,吹塑薄膜 2% secant, TD, 40 µ m, blow molded film |
170 | MPa | ASTM D882 |
2% 正割,MD,40 µm,吹塑薄膜 2% secant, MD, 40 µ m, blow molded film |
140 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
20.0 | MPa | ASTM D882 |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,40 µm,吹塑薄膜 TD, 40 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
60°,40.0 µm,吹塑薄膜 60 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1.0mm Die Gap, 2.0 to 3.0:1 Blow Up Ratio |
【新闻资讯】查看全部
再生资源回收体系不时完善,市场规模超万亿
2018-05-10 1、再生资源回收体系不断完善,市场规模超万亿,回收率仍有提升空间 目前中国已经初步建立起了以回收点、分拣中心和集散交易中心为主的“三位一体”回收链条,同时企业与各地政府正在积极推进环卫系统和再生资源系统的融合,从而提高再生资源以及废塑料的回收效率。 中国2016年主要十大再生资源回收量2.56亿吨,同比增长3.3%;产值5903亿元,同比增长14.5%,其中废电池、废弃电子 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |