公司信息及水印
牌号简介 About |
---|
K38-20-188是一种天然的、紫外线稳定的中等密度聚乙烯管和管树脂,专为天然气分配而设计。当与经批准的INEOS黄色母粒混合时,所得配方(称为K38-20-160)被塑料管道研究所认可为PE2708树脂,具有优异的长期强度和优异的环境应力抗裂性,并通过了ASTM D2513和CSA B137.4材料要求的认证。 K38-20-188 is a natural, UV-stabilized medium density polyethylene pipe and tubing resin designed for natural gas distribution. When blended with an approved INEOS yellow masterbatch, the resulting formulation, known as K38-20-160, is recognized by the Plastics Pipe Institute as a PE2708 resin which exhibits excellent long term strength and outstanding environmental stress crack resistance and is certified to the material requirements of ASTM D2513 and CSA B137.4. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D4883 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.20 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
20 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,F50 10% non-ionic detergent, F50 |
> 5000 | hr | ASTM D1693B |
100%非离子洗涤剂,F50 100% non-ionic detergent, F50 |
> 5000 | hr | ASTM D1693C |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790-A | |
流体静力学设计基础 Fundamentals of Hydrostatic Design |
ASTM D2837 | ||
23℃ 23℃ |
MPa | ASTM D2837 | |
60℃ 60℃ |
MPa | ASTM D2837 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,Area 23℃,Area |
kJ/m² | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
氧感应时间 Oxygen sensing time |
|||
210℃ 210℃ |
min | ASTM D3895 | |
热稳定性 thermal stability |
℃ | ASTM D3350 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Cell Classification Cell Classification |
ASTM D3350 | ||
裂纹缓慢扩展 PENT - Notch Tensile Slow crack propagation PENT - Notch Tensile |
hr | ASTM F1473 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
烟台瞄准化工产业 建设世界一流绿色石化产业基地
2021-06-12 搜料网资讯: 6月3日上午,由中国石油和化学工业联合会、中国化工经济技术发展中心、山东省化专办、烟台市政府联合主办,烟台开发区管委承办的2021年度中国化工园区与产业发展论 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |