牌号简介 About |
---|
Boltaron 9815E大尺寸高冲击65/65额定板材Boltaron 9815F薄膜/板材的配套产品的规格为0.010至0.035英寸。(0.25至89 mm)对于与Boltaron 9815E(挤压)厚规格板相同的飞机内部部件的热成型和二维和三维层压,在配方、性能、防火等级、长度、宽度和无限制颜色可用性方面,Boltaron 9815F(压延)薄膜/板的规格为0.010至0.035英寸。(25至89 mm)两种表面纹理匹配,一种补充9815E。Boltaron 99815F满足联邦航空局对可燃性、烟雾产生和热释放的严格要求,同时具有特殊的物理性能。它具有5.0 ft-lbs/in的抗冲击能力。(265 J/m)-高于竞争性65/65-符合要求的板材,额定值为3.0 ft-lbs/in。(159 J/m)-显著提高热成型和层压飞机内部部件的耐久性。它还提供其他特殊的物理性能,极端的成形性和一致的表面质量,没有夹杂。因此,Boltaron 9815F是由世界领先的商用、军用和私人飞机和直升机制造商、运输公司和内部整修承包商指定的,用于热成型、层压和制造具有无与伦比的耐用性和外观的内部组件。 A companion product to Boltaron 9815E heavy gauge high-impact 65/65-rated sheet, Boltaron, 9815F film/sheet is offered in gauges from .010 to .035 in. (.25 to 89 mm) for thermoforming and two-and three-dimensional laminating of aircraft interior components Identical to Boltaron 9815E (extruded) heavy-gauge sheet in formulation, properties, fire ratings, lengths, widths and unlimited color availability, Boltaron 9815F (calendered) film/sheet is offered in gauges from .010 to .035 in. (25 to 89 mm) in two surface textures that match, and one that complements, 9815E. Boltaron 99815F meets stringent FAA requirements for flammability, smoke generation and heat release while exhibiting exceptional physical properties. It offers Izod Impact resistance of 5.0 ft lbs/in. (265 J/m)- higher than competitive 65/65- compliant sheets rated at 3.0 ft lbs/in. (159 J/m)-significantly improving the durability of thermoformed and laminated aircraft interior components. It also offers other exceptional physical properties, extreme formability and consistent surface quality free of inclusions. As a result, Boltaron 9815F is specified by the world's leading commercial, military and private aircraft and helicopter manufacturers, carriers and interior refurbishing contractors, for thermoformed, laminated and fabricated interior components of unequalled durability and appearance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.49 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
270 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
76.7 | ℃ | ASTM D648 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
3.0E-5 | 1/℃ | ASTM D696 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
放热 exothermic |
FAR 25.853 | ||
2 min 2 min |
kW·min/m² | FAR 25.853 | |
Peak Peak |
kW/m² | FAR 25.853 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Ds Ds |
ASTM F814 | ||
1.5 min 1.5 min |
ASTM F814 | ||
4 min 4 min |
ASTM F814 | ||
成型温度 Forming temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
这个冬天化工原料不饱和树脂涨“疯”了
2017-11-27 11月这个北方进入冬季的季节,是化工原料不饱和树脂行业传统以来的淡季。但是今年的冬季却不简单,国内不饱和树脂产业链表现实在是很抢眼!11月份,不饱和树脂工厂报价累计上调约600-800元/吨。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |