牌号简介 About |
---|
产品说明无机有机填充酚醛模塑料计算机;高耐热性,良好的机械性能,减少了模具收缩和后收缩,不含卤素和有毒重金属。应用领域可涂上电偶工艺、手柄、烹饪炉配件、外壳。 Product Description Inorganically and organically filled phenolic moulding compund; high heat resistance, good mechanical properties, reduced mould shrinkage and post-shrinkage, free of halogens and toxic heavy metals Application Areas handles, cookware fittings, especially designed for chrome and metal plating |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.48 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate 1 |
0.60 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,4hr 23℃,4hr |
15.0 | mg | ISO 62 |
后收缩 Post contraction 2 |
0.25 | % | ISO 2577 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩成型压力 Compression molding pressure |
MPa | ||
压缩成型温度 Compression molding temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
|||
H 961/30 H 961/30 |
MPa | ISO 2039-1 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection |
3 0.079 in/min |
【新闻资讯】查看全部
汽车供应商Haartz进入医用塑料领域
2021-05-13 搜料网资讯: Haartz公司近日宣布收购了Peak Performance Compositing LLC的少数股权。新闻稿称,这一合作关系将使Haartz能够进入快速增长的医药复配市场,增加自身的多元化,并为Peak提供加速 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |