| 牌号简介 About |
|---|
| LL6800N树脂是一种线性低密度聚乙烯，辛烯-1共聚物，溶液法生产，用于吹塑薄膜挤出，具有优良的机械性能。它含有抗阻塞剂、加工助剂和抗氧化剂添加剂。 LL6800N resin is a Linear Low Density Polyethylene for blown film extrusion with excellent mechanical properties. Applications: Heavy-duty bags; liners; LDPE and HDPE blends; packages for general use. Additive: Antiblocking Processing Aid Process: LL6800N resin should be processed on specific extruders for LLDPE. The optimum processing conditions will vary according to the type of equipment used, but the best results are obtained at a melt temperature within the range of 200 to 220° and blends with LDPE with a maximum ratio of 30%. Recommended blow up ratio: 1.8 to 3:1. |
产品描述 Product Description
用途：薄膜;衬里;包装;袋子;混合;
加工条件：吹塑薄膜
性能特点： 抗结块性; 抗氧化; 辛烯共聚单体; High anti-blocking,Inoxidizability,Octene copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.921 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.75 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
TD，断裂，100 µm，吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
|
MD，断裂，100 µm，吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
|||
|
TD，断裂，100 µm，吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
1300 | % | ASTM D882 |
|
MD，断裂，100 µm，吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
% | ASTM D882 | |
|
弯曲模量 Bending modulus |
|||
|
1% 正割，TD，100 µm，吹塑薄膜 1% secant, TD, 100 µ m, blow molded film |
MPa | ASTM D790 | |
|
1% 正割，MD，100 µm，吹塑薄膜 1% secant, MD, 100 µ m, blow molded film |
MPa | ASTM D790 | |
|
落锤冲击 Drop hammer impact |
|||
|
100 µm，吹塑薄膜 100 µ m, blow molded film |
g | ASTM D1709 | |
|
撕裂强度 tear strength |
|||
|
TD，100 µm，吹塑薄膜 TD, 100 µ m, blow molded film |
g | ASTM D1922 | |
|
MD，100 µm，吹塑薄膜 MD, 100 µ m, blow molded film |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，100 µm，吹塑薄膜 60 °, 100 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
100 µm，吹塑薄膜 100 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
镇海炼化提升乙烯裂解炉自动化程度
2017-06-05 6月1日，镇海炼化乙烯裂解炉120个风门的自动调节系统安装完毕，部分投用的风门调节系统大大节省了人力，提高了操作精度和工作效率。 一台裂解炉的风门自动调节系统主要有两个执行器，分别控制南、北两侧的所有风门开度大小，达到调节底部燃料气的燃烧情况的目的。由于每台裂解炉底部风门有36个或48个，数量较多，该系统投用后，将免去频繁人工手动调节，大大减少了操作人员的工作量。 2014年起，烯烃部开始实施自动调节系统改造，当年完成8号裂解炉风门自动调节系统的安装及投用。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付