牌号简介 About |
---|
Formolene® HB5502S1高密度聚乙烯树脂是专为需要优良的刚度和应力抗裂性能的应用而设计的。可用作吹塑树脂或片材挤出热成型树脂。Formolene® HB5502S1符合美国食品和药物管理局在21CFR 177.1520中规定的所有要求,包括用于直接食品接触的聚烯烃制品的安全使用。 Formolene® HB5502S1 HDPE resin is designed for applications requiring excellent stiffness and stress crack resistance properties. It may be used as a blow molding resin or sheet extrusion thermoforming resin. Formolene® HB5502S1 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.955 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
模压成型,F50 Molded into shape, F50 |
35.0 | hr | ASTM D1693B |
100%非离子洗涤剂,模压成型,F50 100% non-ionic detergent, molded, F50 |
45.0 | hr | ASTM D1693A |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,模压成型 Yield, molding 3 |
27.6 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
断裂,模压成型 Fracture, molded 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4, 2,0 in/min |
【新闻资讯】查看全部
邀请函||搜料超市在黄岩博览会A025展位,恭候您的光临!
2023-10-31 扫描上图二维码,可以免费下载 搜料 APP 搜料工程塑料超市诚邀您参加 台州(黄岩)模塑产业博览会 台州(黄岩)机床展览会 我们将在 A025 展位 敬候您的到来 举办时间: 2023年11月 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |