牌号简介 About |
---|
Ultramid® B3L是一种冲击改性,易于流动的注塑成型PA6级快速加工。典型应用包括抗冲击物品,如外壳、配件、小零件和锚。 Ultramid B3L is an impact-modified, easy flowing injection molding PA6 grade for fast processing. Applications Typical applications include impact-resistant articles such as housings, fittings, small parts and anchors. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | ASTM D792 |
密度 Density |
1.10 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
275℃,5 kg 275℃,5 kg |
100 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
1.1 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
9.0 | % | ISO 62 |
饱和 saturated |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
ISO 179 | ||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ |
kJ/m² | ISO 180 | |
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
MD MD |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.8 mm 0.8 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.8 mm 0.8 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.40 mm 0.40 mm |
℃ | UL 746 | |
0.8 mm 0.8 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
资产总额1403亿元!福建省能源石化集团正式成立
2021-08-30 搜料网资讯: 国企改革重组又下一城。刚签下400亿元中沙古雷乙烯项目的福建石化集团与福建能源集团整合重组,正式成立福建省能源石化集团。 福建省国资委网站8月27日消息,福建省 |
资产总额1403亿元!福建省能源石化集团正式成立 搜料网资讯:国企改革重组又下一城。刚签下400亿元中沙古雷乙烯项目的福建石化集团与福建能源集团整合重组,正式成立福建省能源石化集团。 福建省国资委网站8月27日消息,福建省能源石化集团干部大会于8月25日下午召开,宣布了新组建的福建省能源石化集团领导班子任职决定。 重组后,福建省能源集团、福建石化集团成建制划入福建省能源石化集团,集团资产总额1403.02亿元,成为福建省能源、石化产业一体化的龙头企业。 经福建省委研究决定,谢荣兴任福建省能源石化集团有限责任公司党委书记、董事长(法定代表人);徐建平任党委副书记、副董事长、总经理;吴宏任党委副书记、董事;卢范经任党委委员、总会计师;刘强任党委委员、副总经理;柯南进任党委委员;李寿发任党委委员、纪委书记;朱玉武、黄友星、周朝宝任党委委员、副总经理。 下一步,福建省能源石化集团将深入实施国企改革三年行动,加快国有资本布局优化和结构调整,推动打造世界级石化联合体,着力推进科技创新,大力发展清洁能源和节能环保产业,助力实现碳达峰碳中和目标。
资料显示,福建能源集团成立于2009年12月,是由福建省煤炭工业(集团)有限责任公司和福建省建材(控股)有限责任公司整合重组而成,系福建省属国有企业。2020年末资产总额834亿元,净资产352.52亿元;2020年实现营业收入217亿元,利润总额37.5亿元。 福建石化集团于1998年组建的福建省石化产业龙头企业,现有33家一级全资、控股、参股子公司。全资的福建省石油化学工业有限公司与中石化以各50%股比合资设立福建炼油化工有限公司,间接持有福建联合石化有限公司25%股权及福建古雷石化有限公司25%股权。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- 收缩螺丝钉
- 2019-04-26 0
- Ultramid® B3L是一种冲击改性,易于流动的注塑成型PA6级快速加工,UltraMid®B3L在夹具应用中的多功能性决定于树脂的刚度、韧性和摩擦学平衡。
- 阅读全文
收缩螺丝钉
2-典型应用包括抗冲击物品,如外壳、配件、小零件和锚
3-熔体体积流动速率(275℃/5.0 kg),100cm³/10min,ISO 1133
- 塑料收缩螺丝
- 2019-01-25 0
- Ultramid® B3L是一种冲击改性,易于流动的注塑成型PA6级快速加工。典型应用包括抗冲击物品,如外壳、配件、小零件和锚
- 阅读全文
塑料收缩螺丝
2-具有良好的韧性,不易开裂
3-具有良好的耐化性如汽车燃料以及润滑油等
4-流动性能较好,注射成型性好
5-耐高温性能优良
6-耐候性好,紫外线辐射能力强
2-熔体体积流动速率( 275℃,5 kg) 100 cm³/10min
3-弯曲模量(23℃ ) 2500 MPa
4-简支梁无缺口冲击强度( -30℃) 无断裂
5-热变形温度(0.45 MPa,未退火) 160 ℃
6-线性热膨胀系数(MD) 8.5E-5 1/℃
抱歉!暂无数据。