牌号简介 About |
---|
VALOX™ ENH4565树脂33%玻璃纤维增强,无溴无氯阻燃,PBT树脂,抗热震性好,热膨胀系数低。 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.60 | g/cm³ | ASTM D792 |
-- -- |
1.61 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
24 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
250℃,5 kg 250℃,5 kg |
18.0 | cm³/10min | |
265℃,5 kg 265℃,5 kg |
20.0 | cm³/10min | |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD 1 |
% | ||
MD:3.2 mm MD:3.2 mm |
% | ||
TD TD 2 |
% | ||
TD:3.2 mm TD:3.2 mm |
% | ||
吸水率 Water absorption rate |
ISO 62 | ||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 4 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 6 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 7 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 8 |
MPa | ASTM D790 | |
-- -- 9 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 10 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 11 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/2C | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/2U | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 12 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 13 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D4812 | ||
-30℃ -30℃ |
J/m | ||
23℃ 23℃ |
J/m | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 14 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831,ISO 11359-2 | |
MD:-40~150℃ MD:-40~150℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831,ISO 11359-2 | |
TD:-40~150℃ TD:-40~150℃ |
1/℃ | ASTM E831 | |
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 0.20 in/min |
4 类型 1, 0.20 in/min |
5 0.051 in/min |
6 0.079 in/min |
7 Yield |
8 80*10*4 |
9 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
环保部发布第四批环保督查情况汇总表,速来围观!
2017-09-07 经党中央、国务院批准,第四批8个中央环境保护督察组对吉林、浙江、山东、海南、四川、西藏、青海、新疆(含兵团)等省(区)实施督察进驻。截至9月4日,8个督察组均完成第二阶段下沉督察任务。 下沉督察阶段,各督察组高度重视群众环境诉求,及时转办督办群众环境举报,并针对第一阶段督察发现的突出环境问题开展现场调查取证。各地党委、政府高度重视督察整改,借势借力推动解决突出环境问题,加强环保长效机制建设。 山东省通过“过桥 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |