牌号简介 About |
---|
TH53是一种耐热聚丙烯复合产品,其性能优于竞争对手。滑石粉作为无机填料添加到均聚聚丙烯中,可提高强度和耐热性。该产品具有各种基础PPS,如HIPP(高等规聚丙烯或高结晶聚丙烯),并采用汉华道达尔的特殊加工技术制造,以获得高质量和客户满意度。该牌号具有优良的刚性、长期耐热性、抗静电性能和尺寸稳定性。实际应用包括在电气和电子产品零件和家用电器中的应用。 Description Heat-resistant PP compounds are products that outperform the competition. The addition of talc as an inorganic filler to homo-polypropylene provides for enhanced strength and heat-resistance. These products have a variety ofbase PPs, such as HIPP (High Isotactic or High crystalline Polypropylene), and are manufactured with special Hanwha Total processing technology for high quality and customer satisfaction. These grades feature superior rigidity, long-term heat resistance, anti-static property, as Well as dmensional stability. Practical applications include use in electric and electronic product parts and household appliances. Characteristics High heat-resistance and dimensional stability due to use of talc as aninorganic filler; Superior strength ; Superior processability; Superior long-term heat-resistance, and anti-static property. Applications Electric and electronic product exteriors, Dish washers and dish dryers; Coffee maker parts and microwave ovens; Household appliance and industrial products, Food containers, outdoor chairs, outdoor tables. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
13 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:2.0 mm MD:2.0 mm |
0.80 到 1.2 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
34 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
147 | ℃ | ASTM D648 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.20 in/min |
【新闻资讯】查看全部
IBM公司创造了一种压力反响器
2019-02-26 总部位于硅谷的IBM公司最近发明了一种压力反应器。该反应器采用一种名为“Volcat”的新回收方法。Volcat是一种催化化学反应过程,它可“选择性地将”聚酯分解成一种物质,该物质可直接在塑料生产装备中进行喂料,用于生产新产品。 目前,全球每年生产超过2.72亿吨塑料,其中四分之一是由PET制成。 Volcat回收技术旨在采用精准的化学配方、热量和压力组合,来实现塑料的回收利用,减少塑料废弃物的产生。这一技术有彻底改变未来5年来人们丢弃和制造塑料的方式。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |