SABIC® PPcompound 7990E是一种矿物填充改性聚丙烯。这种材料结合了一个非常高的流动性和高刚度,它已经为减少挥发性有机化合物和雾优化。典型的应用包括非美学的汽车内饰和多材料注塑(纺织品二次成型),如门板和内饰。SABIC® PPcompound 7990E是指定的汽车等级。 SABIC® PPcompound 7990E is a mineral filled modified polypropylene.This material combines a very high flow with a high stiffness, it has ben optimized for minimized VOC and FOG. Typical applications include non esthetical automotive interior parts and multi material injection molding (textile overmolding) such as door panels and interior trim. SABIC® PPcompound 7990E is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
30 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
24 hrs 24 hrs |
1.0 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,注塑成型 23 ℃, injection molding |
6.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-40℃,注塑成型 -40 ℃, injection molding |
15 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/4A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-4A | |
0℃,注塑成型 0 ℃, injection molding |
kJ/m² | ISO 180-4A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-4A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM D696 | ||
-30 到 30℃ -30 to 30 ℃ |
cm/cm/℃ | ASTM D696 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ASTM D696 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/5/50 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/5/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ISO 527-2/5/50 | |
拉伸应变 Tensile strain |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ISO 527-2/5/50 | |
弯曲模量 Bending modulus 2 |
|||
注塑成型 injection molding 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 I (三点负荷) |
【新闻资讯】查看全部
金发科技与中海壳牌散装运输项目启动仪式隆重举行
2020-09-08 搜料网资讯:9月6日,金发科技-中海壳牌散装运输项目启动仪式在清远基地隆重举行。金发科技总经理李南京、华南公司总经理戴福乾、供应链总经理袁长长,中海壳牌石油化工有限公 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |