| 牌号简介 About |
|---|
| Vydyne® R533 NAT是通用的33%玻璃纤维增强PA66树脂。可在自然，这是一个注塑等级，是良好的机器饲料，流动和模具释放润滑。与未增强的PA66相比，玻璃增强的Vydyne树脂具有更高的热变形温度、抗蠕变和更好的尺寸稳定性。这些产品对包括汽油、液压油和大多数溶剂在内的各种化学品具有良好的耐化学性。Vydyne® R533 NAT树脂具有略低于铝和锌的拉伸强度和模量性能，由于性能平衡，可以在许多应用中取代这些金属。与铝和/或锌压铸件相比，Vydyne玻璃纤维增强PA66树脂的主要优点是降低生产成本、能耗和零件重量。 Vydyne R533 NAT is general-purpose, 33% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade that is lubricated for good machine feed, flow and mold release. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Vydyne R533 NAT resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-fiber reinforced PA66 resins over aluminum and/or zinc die-cast parts. |
产品描述 Product Description
用途：家电部件;汽车领域的应用;电气/电子应用领域;照明应用;连接器;工程应用;薄壁部件;
颜色：自然色
加工条件：注射成型 Injection Molding
性能特点： 无腐蚀性; 耐腐蚀; 机械强度好; 热稳定性好; 含脱模剂; 尺寸稳定性好; 耐化学性; 润滑性; 电气性好; 易流动; Good Rigidity,Good Dimensional Stability,Good Electrical Properties,Good liquidity,Corrosion Resistant,Good stripping performance,Non-corrosiveness,Lubricating,Solvent resistance,Heat Stabilized
填料：玻璃纤维 33
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.40 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
|||
|
TD TD |
0.90 | % | ISO 294-4 |
|
MD MD |
0.40 | % | ISO 294-4 |
|
吸水率 Water absorption rate |
|||
|
23℃，50% RH 23℃，50% RH |
1.70 | % | ISO 62 |
|
23℃，24hr 23℃，24hr |
0.80 | % | ISO 62 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 | |
|
MD MD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻 Volumetric resistance |
Ω.cm | IEC 60093 | |
|
绝缘强度 Insulation strength |
|||
|
1.00 mm 1.00 mm |
KV/mm | IEC 60243-1 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
All color All color |
HB | UL-94 | |
|
All color All color |
HB | UL-94 | |
|
All color All color |
HB | UL-94 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
|
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
|
灼热丝相对温度 Relative temperature of heating wire |
|||
|
3.00mm 3.00mm |
℃ | IEC 60695-2-12 | |
|
3.00mm 3.00mm |
℃ | IEC 60695-2-12 | |
|
1.50mm 1.50mm |
℃ | IEC 60695-2-12 | |
|
1.50mm 1.50mm |
℃ | IEC 60695-2-12 | |
|
0.75mm 0.75mm |
℃ | IEC 60695-2-12 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
渤海湾首个千亿方气田上部平台开建
2022-05-31 5月27日，记者从中国海油天津分公司获悉，渤中19-6凝析气田I期开发项目中心处理平台(CEPA)组块在青岛场地开工建设，标志着渤海湾首个千亿立方米大气田上部平台正式进入建造阶段。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |