| 牌号简介 About |
|---|
| Braskem Symbios® 4102是一种中等熔融流速的三元共聚物，设计用于生物租赁膜（BOPP）上的热密封层，处理表面的热密封温度低于120℃。本产品不含防滑、防堵剂，可定制配方。本产品适用于金属化工艺。 Braskem Symbios 4102 is a medium melt flow rate terpolymer, designed for use as a heat sealing layer on biorented films (BOPP), with heat seal temperature below 120°C on treated face. This product does not have slip and anti-blocking agents so it is indicated for customized formularization. This product is appropriate for metalizing processes. Applications: Coextrusion of bioriented and conventional film; heat sealable bioriented and conventional film; with a medium temperature of sealing and modifier of properties of conventional film. Also suitable for use in the lamination process. Processing: Bioriented Film (BOPP) Film Coextrusion |
产品描述 Product Description
用途：双向拉伸薄膜;层压板;
加工条件：共挤薄膜
性能特点： 流动性中等; 三元共聚物; Moderate liquidity,Terpolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.902 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
5.5 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD：30 µm，吹塑薄膜 1% secant, MD: 30 µ m, blow molded film |
395 | MPa | ASTM D882 |
|
1% 正割，TD：30 µm，吹塑薄膜 1% secant, TD: 30 µ m, blow molded film |
395 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
屈服，注塑成型 Yield, injection molding |
25.0 | MPa | ASTM D638 |
|
MD，屈服，30 µm，吹塑薄膜 MD, yield, 30 µ m, blow molded film |
MPa | ASTM D882 | |
|
TD，屈服，30 µm，吹塑薄膜 TD, yield, 30 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
屈服，注塑成型 Yield, injection molding |
% | ASTM D638 | |
|
MD，屈服，30 µm，吹塑薄膜 MD, yield, 30 µ m, blow molded film |
% | ASTM D882 | |
|
TD，屈服，30 µm，吹塑薄膜 TD, yield, 30 µ m, blow molded film |
% | ASTM D882 | |
|
始封温度 Initial sealing temperature |
|||
|
30 µm，吹塑薄膜 30 µ m, blow molded film |
℃ | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-20℃，注塑成型 -20 ℃, injection molding |
J/m | ASTM D256 | |
|
23℃，注塑成型 23 ℃, injection molding |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
0.45 MPa，未退火，注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，30 µm，吹塑薄膜 45 °, 30 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
30 µm，吹塑薄膜 30 µ m, blow molded film |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
弯曲模量 Bending modulus |
|||
|
注塑成型 injection molding |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
PA12及其前序安装补充赢创现有生产才能
2019-02-18 德国埃森。赢创已于去年年底如期完成新高性能聚酰胺12(PA12)一体化生产装置的概念性设计和基础工程阶段，现已进入项目实施阶段。该装置计划于2021年上半年投入运营。 该项目耗资约4亿欧元，是迄今为止赢创在德国最大的投资，有望将集团PA12的总产能增加50%以上。新增的PA12及其前序装置将位于北莱茵-威斯特伐利亚的马尔化工园区，补充赢创现有生产能力。 “该项目是一个特殊的挑战。”赢创高性能聚合物业务线负责人Ralf Düssel博士解释说。该业务线产品众多 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付