牌号简介 About |
---|
产品说明TOPAS® 9903D-10是一种非常低的玻璃化转变温度(T g=33°C)薄膜挤出级。它的目的是提供收缩包装应用在低温高收缩。它是一种中等透明度的无定形树脂,具有高硬度、防潮性、耐化学性、热成型性和食品和一般用途的纯度。它用于单层产品中的混合物,单独或多层膜中的混合物。它可用于铸造和吹塑薄膜工艺。主要的薄膜应用是收缩膜和标签。为了提高高温下的性能,建议使用更高的玻璃化转变温度(Tg)等级的TOPA。由于该等级的玻璃化转变温度较低,强烈建议在室温或以下装运和储存球团。选定的应用收缩薄膜和标签食品包装食品接触主要属性低温、低应力、韧性高收缩,不使用双酚A、邻苯二甲酸盐或卤素制造包装和薄膜挤压的广泛法规遵从性相关等级TOPA 9506F-500-坚固低温(T g=65°C)挤压等级TOPAS 9506F-04-高清晰度挤压级 Product Description TOPAS 9903D-10 is a very low glass transition temperature (T g =33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Due to the low glass transition temperature of this grade, shipment and storage of pellets at room temperature or below is strongly recommended. Selected Applications Shrink films and labels Food packaging Food contact Leading Attributes High shrink at low temperatures, low stress, toughness Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 9506F-500 - robust low temperature (T g =65°C) extrusion grade |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ISO 1133 |
230℃,2.16kg 230℃,2.16kg |
3.7 | g/10min | ISO 1133 |
260℃,2.16kg 260℃,2.16kg |
7.4 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
1.00 | cm³/10min | ISO 1133 |
230℃,2.16 kg 230℃,2.16 kg |
cm³/10min | ISO 1133 | |
260℃,2.16 kg 260℃,2.16 kg |
cm³/10min | ISO 1133 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸模量 Tensile modulus |
|||
100 µm,铸造薄膜 100 µ m, cast thin film |
MPa | ISO 527-3/1 | |
拉伸强度 tensile strength |
ISO 527-3/50 | ||
MD,断裂,100 µm,吹塑薄膜 MD, fracture, 100 µ m, blow molded film |
MPa | ISO 527-3/50 | |
TD,断裂,100 µm,吹塑薄膜 TD, fracture, 100 µ m, blow molded film |
MPa | ISO 527-3/50 | |
拉伸应变 Tensile strain |
ISO 527-3/50 | ||
MD,断裂,100 µm,铸造薄膜 MD, fracture, 100 µ m, cast thin film |
% | ISO 527-3/50 | |
TD,断裂,100 µm,铸造薄膜 TD, fracture, 100 µ m, cast thin film |
% | ISO 527-3/50 | |
透氧率 Oxygen permeability |
|||
23℃,100 µm,挤塑薄膜,50% RH 23 ℃, 100 µ m, extruded film, 50% RH |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
100 µm,23℃,铸造薄膜,85% RH 100 µ m, 23 ℃, cast film, 85% RH |
g·mm/m²/atm/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,100 µm,铸造薄膜 60 °, 100 µ m, cast thin film |
ISO 2813 | ||
雾度 Haze |
|||
100 µm,铸造薄膜 100 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
油价一夜暴跌超7%!沙特下调官价引发暴动!
2022-05-13 一、沙特宣布大幅下调原油官价! 近日,沙特阿拉伯公布原油官方售价,其国有公司沙特阿美将销往亚洲的阿拉伯轻质原油的官方售价从较阿曼迪拜均价升水9.35美元/桶下调至升水4.4美 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |