牌号简介 About |
---|
聚丙稀均聚物复合阻燃剂;根据UL94、V0的规范分类,最高可达1.5mm。完全不含卤素和重金属,具有良好的火焰反应性能,在低密度和不透明度条件下,烟气排放量少。具有良好的冲击强度和通用性能,高流动性,适用于电子学领域的注塑成型。可提供自然版,并根据样品上色。 Polyproplene homopolymer compound flame retardanted; classifiable, according to the norms of UL94, V0 up to 1.5mm. Totally halogen and heavy metals free, excellent properties of flame reaction with few emission of smoke at low density and opacity. Good impact strength and general properties, high flowability for injection molding in applications for the electric and electronic field. Available in natural version and colored as per sample. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
15 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.5 | % | ISO 294-4 |
MD MD |
1.5 | % | ISO 294-4 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
20 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加速烘箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
day | ISO 4577 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 335 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
4.0 mm 4.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
针焰测试 Needle flame test 3 |
|||
2.00 mm 2.00 mm 3 |
IEC 60695-2-2 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/20 | |
拉伸应变 Tensile strain |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/20 | |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 Method A-B |
【新闻资讯】查看全部
三星工程与沙特根底签署合同
2017-12-29 三星工程公司已与沙特基础的制造子公司Jubail United Petrochemical Company(美国)签订建设合同,在沙特阿拉伯用7亿美元建设环氧乙烷 - 乙二醇(EO / EG)工厂,生产70万MTPA MEG。 该项目位于沙特阿拉伯东部,位于达曼以北100公里的朱拜勒工业城,预计于2020年完工。 三星工程是全球顶尖EG工厂制造商之一,先前已建16家工厂。三星从沙特阿拉伯提供的27个项目的记录和经验中收益颇多,与22个包括美国在内的沙特基础相 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |