牌号简介 About |
---|
Adflex C 200 F是为坚硬、透明的共挤铸膜结构的中心层开发的。它将透明性与高柔软性、即使在低温下也非常高的韧性以及与其他聚烯烃的良好相容性结合在一起。不含任何滑脱剂和防堵剂。Adflex C 200 F的典型应用是共挤铸造薄膜,用于食品包装、卫生应用、表面保护,其中外层可以是聚烯烃均聚物或共聚物。有关监管信息,请参阅Adflex C 200 F产品管理公告(PSB)。 Adflex C 200 F is developed for the central layer of tough, transparent co-extruded cast-film structures. It combines transparency with high softness , a very high toughness even at low temperatures and an excellent compatibility with other polyolefins. It does not contain any slip nor anti-blocking agents. Typical applications of the Adflex C 200 F are co-extruded cast-film for food packaging, hygiene applications, surface protection where the outside layer can be any polyolefin homo or copolymer. For regulatory information please refer to Adflex C 200 F Product Stewardship Bulletin (PSB). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.890 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
6.0 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3/25 | ||
MD,50 µm,铸造薄膜 MD, 50 µ m, cast thin film |
125 | MPa | ISO 527-3/25 |
TD,50 µm,铸造薄膜 TD, 50 µ m, cast thin film |
110 | MPa | ISO 527-3/25 |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
屈服 yield |
MPa | ISO 527-2 | |
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
断裂 fracture |
% | ISO 527-2 | |
MD,屈服,50 µm,铸造薄膜 MD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,屈服,50 µm,铸造薄膜 TD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
MD,断裂,50 µm,铸造薄膜 MD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,断裂,50 µm,铸造薄膜 TD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
ISO 180/1A | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,铸造薄膜 45 °, 50.0 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中国石化已向粤港澳大湾区供氢超100吨
2021-07-18 搜料网资讯: 7月12日,自2020年12月投产以来,中国石化所属广州石化氢燃料电池供氢中心已向粤港澳大湾区累计供应高纯氢102.15吨,日均出厂量达900公斤,为满足粤港澳大湾区氢能市场 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |