| 牌号简介 About |
|---|
| 行业标准。优良的性能平衡，包括易流动、易加工、热稳定性、耐化学性、机械和电气性能。适用于气相表面安装的电气和电子设备。根据ISO 1043-1，30%玻璃增强化学缩写：LCP固有阻燃塞拉尼斯已在FDA建立了Vectra® MT1310的药物主文件（DMF 8468）和设备主文件（MAF 315）。这些是为了帮助我们的客户最终使用FDA的申请。Vectra® MT1310已经过测试，并符合美国药典第六类。 Vectra® MT1310 VF3001 (natural) is a 30% glass reinforced, easy flow LCP grade for injection molding. Vectra® MT1310 VF3001 (natural) is a special grade developed for medical industry applications and complies with: Food Contact Substance Notification (FCN) No. 742 of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 8464) and the Device Master File (MAF 315) the corresponding EU and national registry regulatory requirements biocompatibility in tests corresponding to USP 23 Class VI/ISO 10993 low residual monomers no animal products The Standard for the Industry. Excellent balance of properties, including easy flow, easy processing, thermal stability, chemical resistance, mechanical and electrical properties. Suitable for vapor phase surface mount electrical and electronic devices. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant |
产品描述 Product Description
用途：电气/电子应用领域;
性能特点： 防火阻燃等级V-0; 热稳定性好; 耐化学性; 阻燃; 易流动; 易加工; Excellent Processability,Good liquidity,Flame Characteristics,Solvent resistance,Heat Stabilized,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.62 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
0.40 | % | |
|
MD MD |
0.20 | % | |
|
吸水率 Water absorption rate |
|||
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
0.040 | % | ISO 62 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
26 | kJ/m² | ISO 179/1eA |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
熔融温度 Melting temperature 1 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
|
MD MD |
1/℃ | ||
|
TD TD |
1/℃ | ||
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
|||
|
1 MHz 1 MHz |
|||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
|||
|
1 MHz 1 MHz |
|||
|
耐电弧性 Arc resistance |
sec | 内部方法 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ISO 2039-2 | ||
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
拉伸蠕变模量 Tensile creep modulus |
ISO 899-1 | ||
|
1 hr 1 hr |
MPa | ||
|
1000 hr 1000 hr |
MPa | ||
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
压缩模量 Compression modulus |
MPa | ISO 604 | |
|
压缩强度 compressive strength |
|||
|
1% 应变 1% strain |
MPa | ISO 604 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部 
Martin Brudermüller接任巴斯夫CEO
2017-12-22 Martin Brudermüller将于2018年接任Kurt Bock，担任执行董事会主席 Kurt Bock被提名为2020年年会监事会主席 Hans-Ulrich Engel将出任执行董事会副主席，并继续担任首席财务官 执行董事会从7人减少至8人 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付