牌号简介 About |
---|
赢创生产一系列聚对苯二甲酸丁二醇酯化合物,这些化合物以注册商标Vestodur提供。表征维托化合物的材料性能为:高耐热性、高刚度、低吸水性,导致高尺寸稳定性、高硬度、高强度、良好的滑动摩擦性能、低磨损、良好的蠕变性能、良好的电气性能、良好的耐化学性、良好的耐候性、良好的加工性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械性能、良好的机械o形成应力裂纹的倾向 Evonik manufactures a range of polybutylene terephthalate (PBT) compounds and supplies it under the registered trademark VESTODUR®. Material properties characterizing VESTODUR® compounds are: high thermostability high stiffness low water absorption resulting in high dimensional stability high hardness good strength good sliding friction behavior, low abrasion good creep behavior good electrical properties good chemical resistance good weathering resistance good processability no tendency to form stress cracks Applications VESTODUR® compounds can be used for a wide range of applications, for example, for thin-walled injection-molded parts in electrical engineering applications, for especially dimensionally stable components of high surface quality in the automotive industry, as a barrier layer in multilayer fuel lines, for laser-markable components, and in the cable industry. High-molecular extrudable VESTODUR® specialty products have come to occupy a leading position as materials for secondary fiber optic jacketing, because they fulfill the requirements perfectly. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.38 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,2.16 kg 250℃,2.16 kg |
23.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.7 | % | ISO 294-4 |
MD MD |
0.40 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.45 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A | |
-- -- |
℃ | ISO 306/B | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength 4 |
|||
1 mm,在油中 1 mm in oil 4 |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
CTI CTI 5 |
V | IEC 60112 | |
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
IEC 60426 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
球压硬度 Ball hardness 3 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
ISO 527-2/50 | ||
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture |
% | ISO 527-2/50 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
可燃性等级 Flammability level |
IEC 60695-11-10, -20 | ||
0.8 mm 0.8 mm |
|||
1.6 mm 1.6 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 H 30 |
3 K 20/P 50 |
4 100 Drops value |
【新闻资讯】查看全部
全球仅9%塑料被回收!经合组织呼吁为再生塑料建立独立市场机制
2022-02-25 每年究竟有多少塑料被回收塑料? 答案是9%!根据经济合作与发展组织(简称经合组织 OECD)本周二发布的一份最新报告《全球塑料展望》(Global Plastic Outlook),目前全球产生的塑料垃 |
全球仅9%塑料被回收!经合组织呼吁为再生塑料建立独立市场机制 每年究竟有多少塑料被回收塑料?答案是9%!根据经济合作与发展组织(简称经合组织 OECD)本周二发布的一份最新报告《全球塑料展望》(Global Plastic Outlook),目前全球产生的塑料垃圾总量大约是20年前的2倍,其中最终大部分被填埋、焚烧或泄露到环境中,只有9%被成功回收。
全球只有9%的塑料被回收。(图片来自OECD) 经合组织是由36个市场经济国家组成的政府间国际经济组织,旨在共同应对全球化带来的经济、社会和政府治理等方面的挑战,并把握全球化带来的机遇。 报告显示,随着人口和收入水平的增加,塑料和使用量和丢弃量也同步增长,遏制塑料泄露到环境中的政策约束力正在下降。 30年来塑料消费量翻两番,废塑料增加一倍多 在新兴市场增长的推动下,塑料消费量在过去 30 年翻了两番。从 2000 年到 2019 年,全球塑料产量翻了一番,达到 4.6 亿吨。塑料占全球温室气体排放量的 3.4%。 与此同时,全球废塑料的产生量增加了一倍多,达到 3.53 亿吨。近三分之二的塑料垃圾来自使用寿命不到五年的塑料,其中 40% 来自包装,12% 来自消费品,11% 来自服装和纺织品。 然而,只有 9% 的塑料废物被回收,其中15% 被收集用于回收, 40% 作为残留物处理。另外19%被焚烧、50% 最终进入垃圾填埋场,22% 逃避废物管理系统并进入不受控制的垃圾场,在露天坑中燃烧或最终进入陆地或水生环境,尤其是在较贫穷的国家中这种情况更为常见。 2019 年,全球有 610 万吨废塑料泄漏到水生环境中,170万吨 流入海洋。现在,海洋中估计有 3000万吨塑料垃圾,另外还有 1.09亿 吨塑料垃圾堆积在河流中。 约50%的废塑料来自于经合组织国家 报告指出,几乎一半的塑料垃圾产生于经合组织国家。每人每年产生的塑料垃圾从美国的 221 公斤和欧洲经合组织国家的 114 公斤到日本和韩国的平均 69 公斤不等。 大多数塑料污染来自于对大塑料碎片的收集和处置不足,但工业塑料颗粒、合成纺织品、道路标记和轮胎磨损等物质中的微塑料(直径小于 5 毫米的合成聚合物)的泄漏也是一个严重的问题。 目前,经合组织国家的塑料泄露量约占全球塑料泄露总量的14%。其中,经合组织国家大塑料泄露占全球的10%,微塑料泄露占全球的35%。 《展望》指出,减少塑料污染的国际合作应包括支持低收入国家发展更好的废物管理基础设施,以减少塑料泄漏。 受新冠疫情影响,2020年全球塑料使用量减少了2.2%,但食品外卖包装和口罩等塑料医疗设备的增加又刺激了使用者乱扔垃圾。随着2021年经济反弹,塑料消费也出现反弹。 禁塑令效果有限 报告认为减少塑料污染需要采取行动和国际合作来减少塑料生产,包括通过创新、更好的产品设计和开发环保替代品,以及努力改善废物管理和增加回收利用。 尽管目前已有120 多个国家/地区对一次性塑料实行禁令和征税,但在减少总体污染方面做得还不够。 这主要是因为大多数法规仅限于塑料袋等物品,它们只占塑料垃圾的一小部分,并且这种遏制塑料消费的行为,并不能像减少乱扔垃圾那样对减少塑料污染更有效。 协调设计方法和化学品监管是关键 考虑到全球价值链和塑料贸易,报告认为协调设计方法和化学品监管将是提高塑料循环性的关键。废物管理的国际方法应调动所有可用的资金来源,包括每年提供约250亿欧元的援助,以帮助低收入和中等收入国家改善废物管理基础设施。 此外,鼓励回收利用的垃圾填埋和焚烧税只存在于少数国家。报告呼吁更多地使用诸如包装和耐用品的生产者责任延伸计划、垃圾填埋税、押金退还和即付即用系统等工具。 再生塑料仅占6%,回收技术可提高二级市场竞争力 值得注意的是,呼声很高的再生塑料,即使从2000年的680万吨增加到2019年的2910万吨,但这仍然仅占塑料总产量的6%。 报告认为需要做更多的工作为再生塑料创建一个独立且运作良好的市场,再生塑料仍被视为原始塑料的替代品。设定回收含量目标并投资于改进的回收技术有助于提高二级市场的竞争力和盈利能力。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。