牌号简介 About |
---|
填充聚丙烯化合物是通过将聚丙烯与细填料(即云母、粉笔、滑石、玻璃)混合而制成的。添加抗氧化剂、润滑剂、加工助剂和干燥剂等添加剂,以改善长期的热加工性能。直接使用或用所需等级的聚丙烯稀释的化合物在最终产品中显示出良好的可溶性和良好的性能平衡。化合物中的填充物具有某些对最终产品至关重要的重要特性。修改如下。 Filled Polypropylene compounds are manufactured by compounding Polypropylene with fine fillers (i.e. mica, chalk, talc, glass). Additives like antioxidants, lubricant, processing aid and desiccant are added to improve long term thermal and processability. The compounds used directly or diluted with desired grades of polypropylenes show good dispensability and excellent balance of properties in the ultimate product. The fillers in the compound incorporates certain important properties those are essential for ultimate product. The modification are as below. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | 内部方法 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
6.5 | g/10min | ASTM D1238 |
含水率 Moisture content |
< 600 | ppm | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
17.2 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
12 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中国物流集团成立 央企专业化重组好戏连台
2021-12-07 搜料网资讯: 12月6日,经国务院批准,中国物流集团有限公司(以下简称中国物流集团)正式成立。这是我国以综合物流作为第一主业的新央企,在我国物流行业发展史上具有里程碑意 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |