牌号简介 About |
---|
HANWHA LLDPE 3322采用滚圆工艺制造,专为重型薄膜设计。LLDPE 3322具有良好的机械性能和加工性能平衡。 HANWHA LLDPE 3322 is manufactured by Spherilene process and designed for heavy duty film. LLDPE 3322 has well balanced property of mechanical property and processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
190 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
断裂 fracture |
20.6 | MPa | ASTM D638 |
MD,断裂,190 µm MD, fracture, 190 µ m |
43.1 | MPa | |
TD,断裂,190 µm TD, fracture, 190 µ m |
MPa | ||
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,190 µm MD, fracture, 190 µ m |
% | ||
TD,断裂,190 µm TD, fracture, 190 µ m |
% | ||
落锤冲击 Drop hammer impact |
|||
190 µm 190 µm |
g | ASTM D1709 | |
撕裂强度 tear strength |
ASTM D1004 | ||
MD,190 µm MD,190 µm |
kN/m | ||
TD,190 µm TD,190 µm |
kN/m | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
190 µm 190 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
北欧化工在2020年提交了182项专利申请记录
2021-03-22 搜料网资讯: 2021年3月17日,北欧化工在2020年向欧洲专利局提交了182项专利申请,打破了上一年的179项纪录。凭借这一成就,北欧化工巩固了其在先进和圆形聚烯烃,塑料,基础化学品 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |