| 牌号简介 About |
|---|
| Plexiglas® HT121是一种热塑性丙烯酸树脂，用于注塑成型。这一等级的耐热性是所有有机玻璃等级中最高的。Plexiglas® HT121具有优异的耐候性和光学性能，使其能够在要求室外稳定性、高质量表面外观和/或精密光学的应用中脱颖而出。它对无机酸、碱和脂肪族碳氢化合物（如vm&p石脑油和庚烷）的溶液具有优异的抗药性。此外，它几乎不受各种商业产品的影响，包括许多饮料、食品、清洁剂溶液和清洁剂。 Plexiglas® HT121 is a thermoplastic acrylic resin formulated for injection molding applications. This grade has the highest heat resistance of all the Plexiglas® grades. Plexiglas® HT121 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VM&P naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners. |
产品描述 Product Description
用途：照明漫射器;汽车领域的应用;
颜色：不透明,可用颜色,半透明,清晰/透明
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 热稳定性好; 尺寸稳定性好; 无BPA; 耐高温; 耐刮擦; 颜色稳定; 透光性好; 收缩性低; 耐候抗UV; Weather resistance is good,Good Clarity,Good Dimensional Stability,Low contractility,Good color stability,High Heat Resistance,No BPA,High scratch resistance,Heat Stabilized,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.19 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，3.80kg 230℃，3.80kg |
2.6 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.20 to 0.60 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.40 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
16 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 2 |
|||
|
1.8 MPa，退火 1.8 MPa, annealed 2 |
℃ | ASTM D648 | |
|
0.45 MPa，退火 0.45 MPa, annealed 2 |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 3 | |
|
-- -- |
℃ | ASTM D1525 4 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index 5 |
ASTM D542 | ||
|
透光率 Transmittance |
|||
|
3180 µm 3180 µm |
% | ASTM D1003 | |
|
雾度 Haze |
|||
|
3180 µm 3180 µm |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
ASTM Classification ASTM Classification |
ASTM D788 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
屈服 yield |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Annealing cycle: 4hrs @ 221°F |
| 3 速率 A (50°C/h), 压 力1 (10N) |
| 4 速率 A (50°C/h), 载荷2 (50N) |
| 5 ND @ 72°F |
|
【新闻资讯】查看全部 
帝人与Fuji Design结成联盟，推进碳纤维回收利用
2022-02-28 帝人有限公司（Teijin Ltd.）与日本再生碳纤维制造商Fuji Design 公司已同意与日本再生碳纤维制造商Fuji Design Co., Ltd.结成商业联盟，以建立一个生产、供应和商业化碳纤维增强塑料（CFRP） |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付