牌号简介 About |
---|
聚酰胺66中粘度30%玻璃纤维增强,阻燃剂UL94V0和5VA额定,热稳定,非常好的防火也在低厚度。高机械和热性能,低收缩和高尺寸稳定性,高跟踪电阻。UL94 V0所有颜色,0.75 mm和5 VA,1.5 mm-UL746 B批准-UL746 A CTI 1级,HAI 0级,HWI 0级标准AFNOR NF F 16-101和NF F 16-102 I2-F3批准用于2 mm黑色。提供:不同颜色。 Polyamide 66 medium viscosity 30% glass fibres reinforced, flame retardant UL94 V0 and 5VA rated, heat stabilized, very good flame proofing also at low thickness. High mechanical and thermal properties, low shrinkage and high dimensional stability, high tracking resistance. UL94 V0 all colours at 0.75 mm and 5VA at 1.5 mm-UL746 B approved-UL746 A CTI class 1, HAI class 0, HWI class 0-Norm AFNOR NF F 16-101 and NF F 16-102 class I2-F3 approved for Black color at 2 mm. Available: different colours. |
产品描述 Product Description
厂家:意大利Taro Plast
类别:PA66 PA66
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级V-0; 热稳定性好; 尺寸稳定性好; 耐电痕; 阻燃; 防火阻燃等级5VA; 收缩性低; Good Dimensional Stability,Low contractility,Flame Characteristics,Heat Stabilized,Electric mark,V-0,5VA
填料:玻璃纤维 30
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.56 到 1.58 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
内部方法 | ||
TD TD |
0.45 到 0.75 | % | 内部方法 |
MD MD |
0.30 到 0.50 | % | 内部方法 |
吸水率 Water absorption rate |
ISO 62 | ||
23℃,24hr 23℃,24hr |
0.50 | % | ISO 62 |
饱和,23℃ Saturation, 23 ℃ |
4.5 | % | ISO 62 |
Granule Humidity Granule Humidity 3 |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 5 |
|||
1.8 MPa,未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature 6 |
℃ | UL 746B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
230℃ 230℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
UL 746 | ||
电气性能,0.75 mm Electrical performance, 0.75 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
3.00 mm 3.00 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
Reaction to Fire Reaction to Fire |
NF F 16-101/102 | ||
烟雾指数 Smoke index |
NF F 16-101/102 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灰份含量 Ash Content 7 |
|||
850℃ 850℃ 7 |
% | ISO 3451 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 TARO 002 |
3 0,039 in/min |
4 120°C/hr |
5 Short Term |
6 1 hr |
【新闻资讯】查看全部 |
保得公司宣布收购原材料供应商公司 美国独特化工品生产商保得公司(Polytek)于昨日公布收购原材料供应商公司(Raw Material Suppliers)。原材料供应商公司为聚氨酯材料、胶黏剂等商品的分销商公司。该次收购有利于保得提高其商品多元性,进一步提高技术实力,为顾客出示更强的服务项目。 来源于:互联网技术 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
第三方认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。