牌号简介 About |
---|
sarlink x23080N是一种高度工程化的热塑性硫化胶,也可作为一种复合母料用于要求严格的汽车和工业应用。Sarlink X23080N是一种中等硬度、低密度等级的材料,具有优异的拉伸强度、优越的压缩永久变形、耐化学腐蚀和高温性能。它可以很容易地通过注塑、挤压或热成型进行加工。 Sarlink® X23080N is a highly engineered thermoplastic vulcanizate that can be used in demanding automotive and industrial applications. Sarlink® X23080N is a medium hardness, low density, RoHS compliant grade with exceptional tensile strength, superior compression set, chemical resistance and high temperature performance. It can be easily processed by injection molding, extrusion, or thermoforming. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.902 | g/cm³ | ASTM D792 |
密度 Density |
0.902 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
TD,100% 应变 TD, 100% strain |
4.20 | MPa | ASTM D412 |
MD,100% 应变 MD, 100% strain |
7.10 | MPa | ASTM D412 |
拉伸强度 tensile strength |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
4.20 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 | |
拉伸强度 tensile strength |
ASTM D412 | ||
断裂 fracture |
MPa | ASTM D412 | |
MD,断裂 MD, fracture |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ISO 37 | ||
断裂 fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture |
% | ASTM D412 | |
流量,断裂 Flow rate, fracture |
% | ASTM D412 | |
拉伸应变 Tensile strain |
ISO 37 | ||
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength |
|||
TD TD 2 |
kN/m | ISO 34-1 | |
TD TD |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395 | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ASTM D2240 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ASTM D2240 | ||
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ISO 868 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ISO 868 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体表观粘度 - Capillary,@ 206/s Apparent viscosity of melt - Capillary, @ 206/s |
|||
200℃ 200℃ |
Pa·s | ISO 11443 | |
200℃ 200℃ |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 方法,直角形试样(不割口) |
【新闻资讯】查看全部
K 2016: 海天推模块化以优化消费
2016-10-28 注塑机制造巨头海天国际的本次K展重点之一是柔性制造。 海天国际在杜塞尔多夫K展现场召开了新闻发布会,公布了模块化生产的新战略,称模块化代表了注塑机设计的演变方向,塑料加工商在选择设备配置时将更加灵活。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |