牌号简介 About |
---|
Lexan Lux7632c树脂Lexan Lux7632c聚碳酸酯(PC)树脂是一种非填充、可挤压级树脂。这种非氯化、非溴化阻燃PC的UL-94V0额定值为1.0 mm/5VA额定值为3.0 mm,并且紫外线稳定(F1额定值)提供了额外的耐候性。Lexan Lux7632C提供扩散色。 LEXAN LUX7632C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is UV stabilized(F1 rating) providing additional weathering capability. LEXAN LUX7632C is available in diffusion colors. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
用途:照明应用;电子显示器;电器用具;
颜色:可用颜色
加工条件:注射成型 Injection Molding
性能特点: 无卤; 防火阻燃等级V-0; 防火阻燃等级V-2; 阻燃; 防火阻燃等级5VA; 耐候抗UV; Weather resistance is good,Halogen free,Flame Characteristics,V-2,V-0,5VA
紫外线:UV Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
5.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.60 to 0.80 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
耐候性 Weathering resistance |
UL 746C | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4812 | ||
-30℃ -30℃ |
ASTM D4812 | ||
23℃ 23℃ |
ASTM D4812 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 9 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,100 mm跨距 1.8 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Ae | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,100 mm跨距 0.45 MPa, unannealed, 100 mm span 9 |
℃ | ISO 75-2/Be | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1.10 GHz 1.10 GHz |
ASTM ES7-83 | ||
耗散因数 Dissipation factor |
|||
1.1 GHz 1.1 GHz |
ASTM ES7-83 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.40 mm 0.40 mm |
UL 94 | ||
1.00 mm 1.00 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1 mm 1 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 120*10*4 mm |
10 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
【全球首款】ALPLA碳中和rPET树脂亮相
2020-10-24 搜料网资讯: ALPLA集团将其位于奥地利W?llersdorf和波兰Radomsko的PET回收团队工厂改为使用可再生能源的混合电力,以生产碳中和的回收聚对苯二甲酸乙二醇酯(rPET)。 这一步已经对我们 |
【全球首款】ALPLA碳中和rPET树脂亮相 搜料网资讯:ALPLA集团将其位于奥地利W?llersdorf和波兰Radomsko的PET回收团队工厂改为使用可再生能源的混合电力,以生产碳中和的回收聚对苯二甲酸乙二醇酯(rPET)。
“这一步已经对我们的食品级再生材料的碳足迹产生了很大的影响——根据计算,与原材料相比,排放量可减少90%,”ALPLA回收部门负责人Georg L?sser解释道,“市场对这一发展的反馈非常好。” 该公司现在向其客户提供附带购买证书的碳中和rPET。例如,与向工厂输送输入材料有关的其他不可避免的排放,将用碳证书来抵消。 L?sser说:“世界上第一款碳中和再生材料可以为气候保护做出重大贡献,并突出废旧塑料的价值。” ALPLA与气候中立联盟Klimaneutralit?tsbündnis 2025和非政府组织Helioz合作选定了具体项目。尼加拉瓜的一个重新造林项目得到了支持。在中国,传统的燃煤炉灶正被以生物质为燃料的炉灶所取代。这不仅大大减少了排放,而且还防止了有害废气对健康产生影响。在埃塞俄比亚,该联盟资助了5000个家庭套餐(现代炉灶、蔬菜种子、幼苗、培训)。在亚洲和非洲地区,ALPLA正在支持Helioz提供太阳能设备,并使用PET瓶监测水的消毒情况。 根据生命周期评估,含有高比例回收材料的包装类型对气候产生的影响最小。作为世界上第一款碳中和rPET,ALPLA正在帮助其客户实现其可持续发展目标。 Lsser总结道:“我们再次证明,包装开发商、包装制造商和回收专家之间的密切合作可以为整个行业树立榜样。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。