牌号简介 About |
---|
UF313采用Unipol工艺技术制造。UF313具有良好的力学性能、光学性能和加工性能。 UF313 is manufactured by Unipol process technology. UF313 has good mechanical properties, excellent optical properties and good processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
43.1 | MPa | ASTM D882 |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
39.2 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength 2 |
ASTM D1922 | ||
MD,40 µm MD,40 µm |
kN/m | ASTM D1922 | |
TD,40 µm TD,40 µm |
kN/m | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
小“茶包”能够会“永远完毕塑料危机”
2019-01-23 塑料污染如今已经是一个让人们不得不面对的话题,而不少公司已经开始有意识地减少了塑料制品的使用。 据外媒报道,一家领先的化妆品公司发明了一种茶包大小的标签状产品,这种标签可能意味着洗发水瓶子的终结。 据宝洁公司(Procter & Gamble)称,这些小“茶包”可能会“永远结束塑料危机”。宝洁是Ariel和潘婷(Pantene)等知名品牌背后的巨头。 这种新的概念,DS3,允许消费者选择一个小的白色“样品”,然后,就像变魔术一样,只要 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |