牌号简介 About |
---|
拜耳5000系列树脂是酸酐改性聚丙烯树脂。它们以颗粒形式提供,用于常规挤出和共挤设备,用于加工聚丙烯(PP)树脂。拜耳5000系列树脂可黏附在各种材料上。它们最常用来粘附在聚丙烯,埃沃和聚酰胺。这些树脂是为EVOH或聚酰胺与PP或PP共聚物熔融共挤而设计的。拜内尔50E806可以纯使用,也可以与聚丙烯混合,以产生对聚酰胺或EVOH等阻隔树脂的粘附力。 BYNEL® Series 5000 resins are anhydride-modified polypropylene resins. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polypropylene (PP) resins. BYNEL 5000 series resins adhere to a variety of materials. They are most often used to adhere to PP, EVOH and polyamide. These resins are designed for applications in which EVOH or polyamide is melt coextruded with PP or PP copolymers. BYNEL 50E806 can be utilized pure, or can also be blended into PP for creating adhesion to barrier resins such as polyamide or EVOH. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.880 | g/cm³ | ASTM D792 |
密度 Density |
0.880 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
25 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
25 | g/10min | ISO 1133 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
100 | ℃ | ASTM D1525 |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
冰点 freezing point |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
2017中国国际机器人产业开展高峰论坛7月在上海举行
2017-06-13 2017年是实施“中国制造2025”的关键一年,由中国机械工业联合会、中国机器人产业联盟主办的2017中国国际机器人产业发展高峰论坛,将于2017中国国际机器人展览会(CIROS 2017)期间再度举办。第二届金手指奖•2017中国机器人产业年度评选颁奖活动也将同期举行。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |