牌号简介 About |
---|
ACRYLITE® Resist ZK6SR聚合物是一种基于聚甲基丙烯酸甲酯(PMMA)的无定形、冲击改性热塑性成型和挤出化合物。丙烯酸酯类聚合物的典型性能有:耐候性高,透光性好,抗应力开裂性能好,熔体流动速率好,易于着色。ACRYLITE® Resist ZK6SR聚合物的特殊性能有:抗冲击性高,抗断裂性强,挤出用高熔体强度,低熔体流动速率,中耐热性,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,耐高温,CA列为ZK6(X)应用:用于挤出片材、共挤片材和挤出型材。 ACRYLITE® Resist ZK6SR polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA). Typical properties of ACRYLITE® Resist acrylic polymers are: high weather resistance high light transmission improved resistance to stress cracking good melt flow rate easy to color The special properties of ACRYLITE® Resist ZK6SR polymer are: high impact/break resistance and strength high melt strength for extrusion low melt flow rate medium heat resistance AMECA listed as ZK6 (x) Application: Used for extruded sheet, co-extruded sheet and extruded profiles. |
产品描述 Product Description
厂家:德国罗姆 ROHM
类别:PMMA PMMA
用途:家电部件;镜头;家用货品;照明应用;文具;胎面胶;外壳;
颜色:清晰/透明
加工条件:共挤出成型
性能特点: 耐热性好; 熔体强度好; 流动性低; 机械强度好; 着色性好; 无定形的; 透光性好; 冲击性能好; 耐候抗UV; Good Rigidity,Weather resistance is good,Good Clarity,Low liquidity,High impact resistance,Good melt strength,Heat Resistance, Good,Good coloring,Amorphous
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | ASTM D792 |
表观密度 Apparent density |
0.71 | g/cm³ | ASTM D1895 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
1.3 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡 balance |
< 0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
0℃,6.4mm 0℃,6.4mm |
J/m | ASTM D256 | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,6.35 mm 1.8 MPa, annealed, 6.35 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:0~100℃ MD:0~100℃ |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
3200 µm 3200 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3200 µm 3200 µm |
% | ASTM D1003 | |
黄度指数 Yellowness index |
|||
3.20 mm 3.20 mm |
YI | ASTM D1925 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
万华化学与天华院联合研发的TDI焦油回收颗粒床干燥机试验成功
2021-08-13 搜料网资讯: 近日,天华院与万华化学集团有限公司共同研究开发的异氰酸酯(TDI)焦油回收颗粒床干燥机试验成功,收率达到98.5%以上,形成的焦油颗粒圆滑光泽,成功具备工业化条 |
万华化学与天华院联合研发的TDI焦油回收颗粒床干燥机试验成功 搜料网资讯:近日,天华院与万华化学集团有限公司共同研究开发的异氰酸酯(TDI)焦油回收颗粒床干燥机试验成功,收率达到98.5%以上,形成的焦油颗粒圆滑光泽,成功具备工业化条件。此次试验的成功,是天华院在聚氨酯(PU)领域的又一次突破。 PU是国民经济生活中不可缺少的新兴材料,性能优越,可广泛应用于家居、建筑、日用品、交通、家电等领域,被誉为国民应用的第六大塑料。TDI是PU最重要的化工原料,而干燥机则是其生产的重要工艺设备。由于TDI产品的高粘性、特殊性和工艺系统的复杂性等特点和难点,其焦油回收颗粒床干燥机及系统长期被国外厂家垄断把持,且价格昂贵。
图为试验分离TDI产品 此次天华院与TDI龙头企业万华化学通力合作,依托天华院国家干燥和装备工程技术研究中心,共同推进TD焦油回收颗粒床干燥机的研发。双方技术人员反复总结交流,出现困难解决困难,没有条件创造条件。经过半年多的现场试验和多次的设备改造,终于成功产出产品。经检测,产出产品质量明显优于进口设备品质,为TDI焦油颗粒床干燥机设备和干燥回收系统的进一步工业化国产化奠定了重要基础。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。