牌号简介 About |
---|
G-Blend 65/85/85Hi是一种基于聚碳酸酯和丙烯腈-丁二烯-苯乙烯的无增强、无定形热塑性聚合物混合物。它以其韧性、刚度和易流动、易成型而著称。这种混合物含有一定比例的再生材料和原材料,以生产出性能优异的聚合物,与同等的原材料相比,给用户带来相当大的成本降低的好处。G-Blend 65/85/85HI符合所有回收指令,可正常回收。典型应用包括汽车内饰、手机外壳、电气和电子外壳以及一些家用产品。这种材料有黑色、天然色和各种颜色。 G-Blend 65/85/85HI is a non-reinforced, amorphous thermoplastic polymer blend based on polycarbonate and acrylonitrile butadiene styrene. It is noted for its toughness, rigidity and ability to flow and mould easily. This blend contains a proportion of recycled and prime material to produce a polymer that offers outstanding properties, giving users the benefit of considerable cost down over equivalent prime grades. G-Blend 65/85/85HI complies with all the recycling directives and can be recycled in the normal way. Typical applications include interior automotive trim, mobile phone housings, electrical and electronic enclosures and some household goods. This material is available in a black and natural and a whole range of colours. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
15 | g/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
0.50 到 0.70 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
平衡,23℃,85% RH 平衡,23℃,85%RH |
0.18 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2200 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/50 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 500 bar |
【新闻资讯】查看全部
IEA释放6000万桶石油储备!美油新高后,美联储将如何加息?
2022-03-02 投资者忧虑对俄制裁加码恐令原油出口受阻,加剧本就失衡的全球石油供应,WTI原油期货周二盘中暴力拉升11.5%,逼近107美元/桶,创2014年6月以来新高;布伦特原油期货一度大涨近一成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |