牌号简介 About |
---|
Nucrel® 0609HSA是乙烯和甲基丙烯酸的共聚物,通常由6.5 wt%的甲基丙烯酸制成。它包括一种抗氧化剂。该树脂可用于传统的挤出涂料、共挤涂料和设计用于加工聚乙烯树脂的挤出复合设备。 Nucrel® 0609HSA is a copolymer of ethylene and methacrylic acid made with nominally 6.5 wt% methacrylic acid. It includes an antioxidant. The resin is available for use in conventional extrusion coating, coextrusion coating and extrusion laminating equipment designed to process polyethylene resins. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ASTM D792 |
密度 Density |
0.930 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
9.0 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
9.0 | g/10min | ISO 1133 |
Methacrylic Acid Content Methacrylic Acid Content |
6.5 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
冰点 freezing point |
|||
-- -- |
℃ | ISO 3146 | |
-- -- |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
恭喜!科莱恩选择性催化剂助力宝来年产100万吨乙烯装置成功开车
2020-09-18 搜料网资讯: 科莱恩选择性加氢催化剂助力宝来年产100万吨乙烯装置成功开车。 该C2加氢反应器开车期间快速平稳,从裂解气进C2加氢反应器到出口乙炔合格仅用了不到4个小时,显示出 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |