云母增强酚醛模塑料主要用途:换向器本产品符合重金属和PCA的允许上限,也符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)的要求。 Mica reinforced phenolic moulding compound Primary applications: Commutators This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.65 到 1.75 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 到 0.90 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate 2 |
|||
MD MD 2 |
0.30 到 0.50 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.10 | % | ISO 62 |
后收缩 Post contraction 3 |
0.10 到 0.20 | % | ISO 2577 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
模压成型 Compression Molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
模压成型 Compression Molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~150℃ MD:50~150℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.5 mm,Tested by Synres-Almoco 1.5 mm,Tested by Synres-Almoco |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
3 168 h / 110°C |
【新闻资讯】查看全部
2018年塑料机械行业:深化展开智能化技术
2018-01-05 塑料,作为轻工业行业里的巨人,每年为世界经济的发展贡献巨大的力量。中国作为重要的塑料生产和消费大国,更是在塑料产业发挥着巨大的作用。随着我国社会经济、市场规模和科学技术的发展,我国政府及时调整和更改经济战略,按中国国情制定发展规划,深入发展具有中国特色的社会主义市场经济。 《中国制造2025》、“十三五”规划和国家发改委于2017年12月26日印发的《增强制造业核心竞争力三年行动计划(2018-2020年)》都表明我国加快建设制造强国和发展先进制造业的决心。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |