牌号简介 About |
---|
说明ECO溶液GP3002是一种聚乳酸基脂肪族聚酯,经认证为可生物降解树脂,符合ASTM D6400、EN13432。加工性能和韧性都有了很大的提高,因而在吹炼机中易于引入。一种新的更硬的添加剂,专门开发用于生物基和生物降解包装。GP3002,它使聚乳酸包装材料变得坚韧,同时保持符合美国食品接触要求。它提供的韧性只会使包装的清晰度降低到最低程度,据说这一等级可以使食品营销人员更好地利用包装中的环境优选解决方案,如用于新鲜农产品的蛤壳。方法。应用卓越的侧面密封和端部密封性能高质量薄膜用于瓶子的自动包装过程吹塑半透明袋、面包袋、信封袋、聚乳酸纤维增强塑料高质量薄膜的层压。 Description Eco Solution GP3002 is a PLA (polylactide) based Aliphatic Polyester, and is certified as a biodegradable resin and meet ASTM D6400, EN13432. The processibility and toughness are greatly improved and thus can be leaded in blowing machine readily. A new tougher additive specially developed for bio-based and biodegradable packaging. GP3002, which toughens PLA packaging materials while maintaining compliance with food contact requirements in the U.S. Providing toughness with only minimal reduction in package clarity, this grade is said to allow food marketers to take better advantage of environmentally preferred solutions in packages such as clamshells used in fresh produce sections. Applications Outstanding side sealing and end sealing performance High quality films for automatic packing process Blowing molding for bottles Translucent bags, bakery bags, envelope bags PLA toughner High quality film for lamination |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.26 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.5 到 5.6 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
MD MD |
965 | MPa | ASTM D882 |
TD TD |
480 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
28.4 | MPa | ASTM D882 |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | JIS K6781 | |
TD,断裂 TD, fracture |
MPa | JIS K6781 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
以废聚苯乙烯消费封堵护壁剂FPS隔离膜
2016-04-21 以废聚苯乙烯为原材料研发的致密性强、韧性大的仿沥青封堵护壁剂FPS,用于生产隔离膜。 中原石油工程公司钻井工程技术研究院研发出仿沥青封堵护壁剂FPS,性能优于目前最常用的改性沥青类材料,该护壁剂以废聚苯乙烯(PS)泡沫等为主要原料。 FPS是研制的微裂缝封堵用乳胶护壁材料。该材料以废聚苯乙烯泡沫塑料为主要原料,性能优于目前最常用的改性沥青类材料FPS外观为白色胶乳,无荧光,粒径在0.1~10微米,0℃以上就能使用,抗温可达200℃,所形成的隔离膜致密性强、韧 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |