牌号简介 About |
---|
食品包装用白色金属化固体基共轴双向拉伸聚丙烯薄膜单面密封 Solid White Metalizable Base CoEx BIAXIALLY ORIENTED POLYPROPYLENE FILM ONE SIDE SEALABLE FOR FOOD PACKAGING |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability 2 |
|||
TD,130℃ TD,130℃ |
< 3.0 | % | |
MD,130℃ MD,130℃ |
< 5.0 | % | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
17 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
138 | MPa | ASTM D882 |
TD,屈服 TD, yield |
221 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
氧气传输速率 Oxygen transfer rate |
|||
22℃,0% RH 22℃,0% RH |
cm³/m²/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1249 | |
用量 dosage 3 |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
不透明 Opaque |
% | ASTM D589 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Seal Temperature Heat Seal Temperature 4 |
℃ | ||
表面能 Surface energy |
dyne/cm | ASTM D2578 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5 minutes |
3 Internal Method |
4 1/2 sec, 30 PSI |
【新闻资讯】查看全部
茂名石化合成树脂新产品开发加快
2016-07-20 上半年,茂名石化加大科研创新投入,通过调整合成树脂产品结构,在三元共聚聚丙烯、顶替进口合成树脂新产品等方面开展攻关,增产适销对路且附加值高的产品。 该公司化工新产品累计总产量为8.53万吨,完成总部下达计划的68.46%,超进度完成计划。合成树脂产品中新产品占比达到9.85%,高密度大中空IBC桶专用料TR580等3个新产品产销量达到万吨级。 上半年,已完成15个新产品的研发工作,其中,“汽车用高抗冲聚丙烯K9010H”等7个新产品实现了工业化试生产,并获得 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |