牌号简介 About |
---|
应用Eltex® PF6130AA特别适用于单层和共挤结构中的高性能铸造拉伸膜应用。也可用于人工草单膜的制作。其优点和特点是Eltex® PF6130AA是一种含己烯-1的聚乙烯共聚物,它是用茂金属催化剂制备的共聚单体。Eltex® PF6130AA具有以下特性:在铸膜应用中具有很高的拉伸性、高的保持力、挤压过程中良好的纸幅稳定性、高的输出速率、优异的整体薄膜外观和表面光洁度、极高的抗穿刺性。 Applications Eltex® PF6130AA is particularly suitable for high performance cast stretch film applications, in both monolayer and co-extruded structures. It also can be used for the production of artificial grass monofilmaments. Benefits and Features Eltex® PF6130AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. Eltex® PF6130AA offers the following properties: High stretchability in cast film applications High holding force Good web stability during extrusion High output rates Excellent overall film appearance and surface finish Very high puncture resistance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1872-1 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.5 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
膜刺穿能量 Membrane puncture energy |
|||
20 µm 20 µm |
0.280 | J | Internal Method |
拉伸模量 Tensile modulus |
ISO 1184 | ||
1% 正割,MD,20 µm 1% secant, MD, 20 µ m |
115 | MPa | ISO 1184 |
1% 正割,TD,20 µm 1% secant, TD, 20 µ m |
MPa | ISO 1184 | |
拉伸强度 tensile strength |
ISO 1184 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ISO 1184 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ISO 1184 | |
拉伸应变 Tensile strain |
ISO 1184 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ISO 1184 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ISO 1184 | |
落锤冲击 Drop hammer impact |
|||
20 µm 20 µm |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD,25 µm MD,25 µm |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD,25 µm TD,25 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm 45°,20 µm |
ASTM D2457 | ||
雾度 Haze |
|||
20 µm 20 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
东京及冲绳初次在贝类体内检出微塑料
2018-06-19 据日媒报道,日前,日本东京农工大学教授高田秀重等的团队确认,在东京湾和冲绳县座间味岛海岸的双壳纲生物体内,大量积蓄了成为全球规模海洋污染问题的“微塑料”。 资料图:贝壳。 据报道,该团队称,微塑料过去曾在东京湾的�鱼体内发现,而贝类仅在海外有过检出微塑料的先例。目前,在双壳纲生物体内,容易被生物摄入体内的直径0.02至0.08毫米的微小粒子较多,团队指出:“有必要详细调查对贝 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |