牌号简介 About |
---|
Tuffoly 4270是一系列具有热塑性性能的液体成型化合物,如高冲击、高热变形和低粘度。这种独特的化学产品由HAPCO开发,以满足当今市场对原型和低产量零件的需求。Tuffally 4270系列有(4)种速度。用户可以使用不同速度的Tufflory 4270,通常最初使用较慢的速度,并增加到一个快速设置,1分钟的工作寿命。加工:Tuffoly 4270系列可采用压力铸造、真空铸造或敞口铸造。为了达到最佳效果,Tuffally 4274/75应与Hapco的计量/分配设备、RapidFil、Mini Fil和RapidShot一起使用。 TUFFALLOY 4270 is a series of Liquid Molding Compounds with thermoplastic properties such as high impact, high heat distortion, and low viscosity. This unique chemistry developed by Hapco to meet today's market demands for prototype and low production parts needs. THE TUFFALLOY 4270 Series are available in (4) speeds. The user has the ability to use different speeds of TUFFALLOY 4270, typically using a slower speed initially and increasing to a fast set, 1 minute working life. PROCESSING: TUFFALLOY 4270 Series can be pressure cast, vacuum cast, or open cast. For best results, TUFFALLOY 4274/75 should be used with Hapco's metering/dispensing equipment, RAPIDFIL, MINI FIL, and RAPIDSHOT. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D4669 |
收缩率 Shrinkage rate |
|||
MD MD |
0.050 到 0.30 | % | ASTM D2566 |
Weight(per cubic inch) Weight(per cubic inch) |
19 | g | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
80 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
> 110 | J/m | ASTM D256 |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ 2 |
cP | ASTM D4878 | |
脱模时间 stripping time |
|||
21℃ 21℃ |
min | 内部方法 | |
胶凝时间 Gelation time 3 |
|||
25℃ 25℃ 3 |
min | ASTM D2971 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Range: 250 to 350 |
3 100 g |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |