牌号简介 About |
---|
Kalix® 2955是一种生物来源的、以聚酰胺为基础的化合物,其重量百分比为55%的玻璃纤维增强材料。这种材料是专门为高强度和刚度应用而设计的,在这些应用中,要求具有良好的抗冲击性和成型后的良好尺寸稳定性。该公式还解决了与玻璃纤维增强材料的各向异性收缩有关的翘曲问题,以便更容易实现精密公差成型。它的低粘度和优良的流动性能使这种材料非常适合于填充具有薄壁截面的部件,如移动电子工业中遇到的部件。黑色:Kalix® 2955黑色000白色:Kalix® 2955白色000 Kalix® 2955 is a bio-sourced, polyamide-based compound with 55% by weight glass fiber reinforcement. This material is specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry. Black: Kalix® 2955 BK 000 White: Kalix® 2955 WH 000 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.58 | ||
收缩率 Shrinkage rate 2 |
内部方法 | ||
TD TD |
0.30 | % | 内部方法 |
MD MD |
0.090 | % | 内部方法 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.090 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
17800 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
断裂弯曲应变 Fracture bending strain |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant 3 |
|||
2.40 GHz 2.40 GHz 3 |
ASTM D2520 | ||
耗散因数 Dissipation factor 3 |
|||
2.4 GHz 2.4 GHz 3 |
ASTM D2520 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
> 0.60 mm,黑色,白色 >0.60 mm, black, white |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 索尔维测试方法。收缩率会根据部件的设计和加工条件而改变。请接洽索尔维技术代表,获取更多信息。 |
3 方法 B |
【新闻资讯】查看全部
PET在碳酸软饮料与瓶装水运用日益广泛
2016-03-22 PET制造商DAK Americas预期今年在墨西哥GDP水平的增长,能在碳酸软饮料到瓶装水中用到更多的PET。对于DAK和其他PET制造商来说都看到了这个一个变化,那就是每单位瓶装水比软饮料瓶运用更少的PET。 据业务主管Antonio Garza Rios预测,2016年墨西哥PET需求量将增长约2.5%,这完全符合墨西哥的经济情况,Garza Rios指出墨西哥曾经是一个人均软饮料消费领先的国家,直到2014年苏打水税的颁布,该国的软饮料消费在第一年就下降了12%。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |