牌号简介 About |
---|
Menzolit® SMC 1000是一种基于不饱和聚酯树脂的片状模塑料。该产品是玻璃纤维增强,含有矿物填料。如果发生火灾,产品不会熔化,也不会形成液滴,也不会产生过量的烟雾。这种材料是在加热的钢模中压缩成型的。建议使用镀铬工具。该产品不含卤素。Menzolit® SMC 1000是一种用于抗水解应用的特殊SMC。选择玻璃料位是为了将良好的塑性与良好的强度和刚度性能结合起来。典型应用是暴露在水或湿气中的部件。这可能是暴露在热带气候或潮湿植物环境中的外壳、盖子和类似部件,导致大量浸入水中或暴露在高湿度环境中。分段水箱面板是另一个非常典型的应用。 Menzolit® SMC 1000 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 1000 is a special SMC for hydrolysis resistant applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Typical applications are components facing exposure to water or moisture. This may be housings, covers and similar components exposed to a tropical climat or humid plant environment causing extensive immersion in water or exposure to high humidity. Sectional watertank panels are another very typical application. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.70 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
-- -- 1 |
0.0 | % | DIN 53464 |
-- -- |
0.080 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
< 0.30 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
模压成型 Compression Molding |
11000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
模压成型 Compression Molding |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature |
℃ | 内部方法 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Glow Bar Glow Bar |
IEC 60707-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Post Molding Shrinkage |
【新闻资讯】查看全部
宁东基地第三批重大项目集中开工
2021-08-07 搜料网资讯: 7月30日,宁东基地第三批重大项目集中开工。 据了解,此次集中开工的重大项目共23个,涵盖产业发展、基础设施建设、生态环保等,总投资40亿元;2021年计划投资约5亿元 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |