Smooth-On MT-13®是一种高性能环氧树脂,适用于需要最大保持力和耐水性的应用场合。MT-13是一种双组分环氧胶粘水泥,按体积(100A/123B,按重量)等份混合,几个小时后形成凝胶。它在16小时内提高了处理强度,并非常好地粘附在多孔和非多孔表面上。MT-13广泛应用于船舶工业的装配和一般修理。在极端寒冷的条件下,MT-13还保持着保持动力。 Smooth-On MT-13® is a premium performance epoxy for applications requiring maximum holding power and water resistance. MT-13® is a two component epoxy adhesive cement which is mixed in equal parts by volume (100A/123B by weight) and gels in a few hours. It develops handling strength in 16 hours and adheres extremely well to both porous and non-porous surfaces. MT-13® is widely used by the boating industry for assembly and general repair. MT-13® also maintains holding power under extreme cold conditions. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.37 | g/cm³ | |
粘度 viscosity |
Light-paste | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
|||
23℃ 23℃ |
35 | min | |
脱模时间 stripping time |
|||
23℃ 23℃ |
960 | min | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
1A:1B by volume 100A:123B by weight | ||
Sag Resistance Sag Resistance |
mm | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
总投资约330亿元!永盈新材年产80万吨功能性新材料项目一期开工
2022-07-04 据南充市政府网站介绍,6月30日上午,永荣控股集团与南充合作项目一期永盈新材料年产80万吨功能性新材料综合产业链项目在南充经济开发区正式启动。 据搜料网了解,年产80万吨功 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |