MVR(300°C/1.2 kg)6.0 cm³/10 min;10%玻璃纤维增强;阻燃;UL 94V-0/1.5 mm和5VA/3.0 mm;高粘度;紫外线稳定;易释放;注塑-熔融温度310-330°C;仅提供不透明颜色 MVR (300 °C/1.2 kg) 6.0 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; UV stabilized; easy release; injection molding - melt temperature 310 - 330 °C; available in opaque colors only |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ISO 1183 |
表观密度 Apparent density 2 |
0.64 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
7.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
6.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.40 to 0.60 | % | ISO 2577 |
MD MD |
% | ISO 2577 | |
TD:2.0 mm TD:2.0 mm 3 |
% | ISO 294-4 | |
MD:2.0 mm MD:2.0 mm 3 |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 6 |
|||
23℃,完全断裂 23 ℃, completely fractured 6 |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃,完全断裂 -60 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 7 |
|||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
136℃ 136℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient 8 |
|||
23℃ 23℃ 8 |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm,本色,黑色,灰色 3.00 mm, natural color, black, gray |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 9 |
% | ISO 4589-2 | |
小型燃烧器火焰的应用 The Application of Small Burner Flames |
|||
Method K and F,2.00 mm Method K and F,2.00 mm |
DIN 53438-1, -3 | ||
燃烧速率 Burning rate |
|||
USFMVSS,> 1.00 mm USFMVSS,> 1.00 mm |
ISO 3795 | ||
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
23℃ 23℃ |
IEC 60426 | ||
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/5 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0.079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 Based on ISO 180-A, 3 mm |
8 Cross-flow |
9 程序 A |
【新闻资讯】查看全部
未来,塑料工业有哪些市场值得关注?
2018-03-08 机械、包装、材料、薄膜、石化和原料等领域与塑料行业有着千丝万缕的联系,彼此之间有着或强或弱的相互作用关系。终端需求影响上游制造,随着行业跨领域经营逐步加深和融合,塑料工业呈现出了更加多元化、多样化和多领域化的发展状况。这为塑料工业发展带来更强劲的生命力和活力,也赋予其更加光明的未来。 |
未来,塑料工业有哪些市场值得关注? 机械、包装、材料、薄膜、石化和原料等领域与塑料行业有着千丝万缕的联系,彼此之间有着或强或弱的相互作用关系。终端需求影响上游制造,随着行业跨领域经营逐步加深和融合,塑料工业呈现出了更加多元化、多样化和多领域化的发展状况。这为塑料工业发展带来更强劲的生命力和活力,也赋予其更加光明的未来。 未来,塑料工业有哪些市场值得关注? 全球经济持续回暖,带动全球各领域经济复苏,拉动全球资金流动,全球经济市场活力上升;再加之新兴科技领域发展,这意味着未来塑料工业发展机遇良多,行业转型升级、企业发展壮大都要把握好时间与机会!那么,塑料工业和有关企业发展要注意哪些领域呢? 塑料薄膜市场 我国塑料薄膜产业增速平稳,2010-2016年我国塑料薄膜产量由799万吨增加至1419万吨,年均复合增速达10%;2017年全球液晶聚合物薄膜和层压板销售量约9050吨,复合年增长率为6.7%。快递包装薄膜将呈现减量化、绿色化、可循环发展趋势;背光模组光学膜将趋于高亮度化、薄型化、轻量化、高色域化发展。 瓶装水市场 碳酸软饮料等销量逐年降低,有关数据显示,碳酸软饮料已经持续十多年销量下降,而瓶装水,尤其是一次性PET瓶装水,自90年代初以来一直在增长,这一趋势预计将继续保持。 车用塑料材料市场 Global Market Insights,Inc.最新研究报告显示,2024年全球汽车复合材料市场需求预计将达400万吨,市场总值将达到240亿美元。 填料市场 市场调研公司Ceresana最新调研报告指出,全球重质碳酸钙(GCC)、沉淀碳酸钙(PCC)、高岭土、云母、炭黑和其他填料的市场需求到2024年预计达到7500万吨。 石化市场 2017年,中国深化供给侧结构性改革,大力推进创新驱动和转型升级,石化化工行业主营业务收入增长15.8%,行业发展迈向崭新阶段。 新材料市场 工信部发布消息称,我国新材料产业发展势头良好,并将保持这良好的增长势头,预计到2025年产业总产值将达到10万亿元,并保持年均增长20%。 包装市场 美国有研究公司调查研究显示,到2021年,包装市场对于PET薄膜的需求将增长2.4%,达到3.22亿磅,将超过对任何包装树脂的需求。 小结 塑料已成建筑、电子、电器和包装等领域必需的材料之一,影响着人们的日常生活和生产,今后,塑料工业将以创造为动力,来满足国民经济各部门的需求和发展。 来源:中国塑料机械网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。