| 牌号简介 About |
|---|
| TENITE纤维素塑料以其优良的性能平衡而闻名——韧性、硬度、强度、表面光泽、透明度和温暖感。细纤维素塑料的力学性能随增塑剂用量的不同而不同。增塑剂含量越低，表面越硬，耐热性越高，刚性越高，拉伸强度越高，尺寸稳定性越好。增塑剂含量越高，冲击强度越高。Tenite纤维素塑料有天然、透明、精选的琥珀色或烟雾透明和黑色半透明。颜色浓缩物可按10:1到40:1的比例稀释。醋酸丁酸纤维素285-18的增塑剂含量为18%，含有防臭面具。 Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulose plastics are available in natural, clear, selected ambers, or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 285-18 has a plasticizer level of 18% and contains an odor mask. |
产品描述 Product Description
用途：镜架;眼镜;安全设备;
颜色：琥珀色,黑色,清晰/透明,自然色
性能特点： 可回收; 经增塑; 机械强度好; 柔软性好; 硬度高; 透光性好; 韧性好; 表面光泽度好; Good Rigidity,Good Clarity,Good flexibility,Good surface appearance,Renewable resources,Good Hardness,Soft,Plasticizing
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.17 | g/cm³ | ASTM D792 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
1.3 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-40℃ -40℃ |
110 | J/m | ASTM D256 |
|
23℃ 23℃ |
360 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 2 |
|||
|
1.8 MPa，退火 1.8 MPa, annealed 2 |
61.0 | ℃ | ASTM D648 |
|
0.45 MPa，退火 0.45 MPa, annealed 2 |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp 2 |
℃ | ASTM D1525 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
可溶性物质损失 Loss of soluble substances |
|||
|
23℃ 23℃ |
% | ASTM D570 | |
|
加热减量 Heating reduction |
|||
|
72 hrs，80℃ 72 hrs，80℃ |
% | ASTM D707 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Conditioned 4 hours at 70°C (158°F) |
|
【新闻资讯】查看全部
陕西成为全国煤制烯烃第一大省 总产能310万吨
2016-02-02 1月31日来自省工信厅消息，随着神华集团榆神60万吨烯烃项目建成，陕西煤制烯烃总产能将达到310万吨，成为全国煤制烯烃第一大省。 “十二五”期间，我省在现代煤化工和精细化工等领域建成了4个大型煤制烯烃项目，10个煤制油项目，目前已形成榆神、榆横2个千亿级大型现代化工产业集中区。预计到2020年，我省将建成现代煤化工项目11个，转化煤炭5000万吨，形成约1000亿元的产值规模。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名：搜料网-Tenite™ Butyrate 285A2R30018 Natural, Trsp证书
发送至：（多个地址，中间以逗号隔开）
发送一份副本给我：您还没有填写邮箱!(点击完善资料)
当前牌号已加入对比
支付宝
微信支付